Prepregs, cores, composites and articles including repellent materials

ABSTRACT

Prepregs, cores and composite articles are described that comprise lighter weight materials and/or lower amounts of adhesive than commonly used. In some instances, one or more components of the articles may comprise a repellent material or repellent treatment to reduce the overall absorption rate of adhesive into the components of the article.

PRIORITY APPLICATION

This application claims priority to, and the benefit of, U.S.Provisional Application No. 61/879,066 filed on Sep. 17, 2013, theentire disclosure of which is hereby incorporated herein by reference.

TECHNOLOGICAL FIELD

This application is related to prepregs, composites and articles thatcan be produced using one or more repellent materials to permit the useof lesser amounts of adhesive, lighter weight materials or provide otherdesirable attributes.

BACKGROUND

Porous fiber-reinforced thermoplastic composite sheets are described inU.S. Pat. Nos. 7,244,501 and 7,628,697.

SUMMARY

In one aspect, a prepreg comprising a thermoplastic material and aplurality of reinforcing materials dispersed in the thermoplasticmaterial to provide an open cell structure is described. In certainconfigurations, the prepreg further comprises a repellent treatment onat least one surface of the prepreg, the repellent treatment effectiveto decrease absorption of a fluid into the open cell structure of theprepreg, e.g., fluid absorption is less or slower as compared to acomparable surface with no repellent treatment.

In certain instances, the reinforcing materials comprise reinforcingfibers. In other instances, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the prepreg. In some embodiments, the reinforcing fibers comprisemetal fibers, metalized inorganic fibers, metallized synthetic fibers,glass fibers, carbon fibers, aramid fibers, ceramic fibers andcombinations thereof. In other embodiments, the prepreg may furthercomprise an adhesive layer disposed on the at least one surfacecomprising the repellent treatment. In some configurations, the adhesivelayer comprises a polyolefin adhesive, an ethylene-vinyl acetateadhesive, a polyamide adhesive, a polyester adhesive, a polyurethaneadhesive, a thermoplastic polyurethane adhesive, a styrene blockcopolymer adhesive, a polycarbonate adhesive, a fluoropolymericadhesive, a silicone adhesive, a silicone rubber adhesive, anelastomeric adhesive, or a pyrrole adhesive. In other instances, theprepreg further comprises a substrate disposed on the adhesive layer. Insome instances, the repellent material is effective to render theadhesive temperature insensitive. In other instances, the thermoplasticmaterial of the prepreg comprises polyethylene, polypropylene,polystyrene, acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, polyvinylchloride, polyphenylene ether, polycarbonates, polyestercarbonates,thermoplastic polyesters, polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some embodiments, the prepreg may comprise aflame retardant. In some configurations, some portion of a surface ofthe prepreg comprises a repellency grade number of at least 3 as testedby ISO 23232 dated 2009.

In another aspect, a prepreg comprising a thermoplastic material and aplurality of repellent treated reinforcing materials dispersed in thethermoplastic material to provide an open cell structure is disclosed.In certain instances, the repellent treated reinforcing materials areeffective to decrease absorption of a fluid into the open cell structureof the prepreg.

In certain embodiments, the reinforcing materials comprise reinforcingfibers. In other embodiments, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the prepreg. In further instances, the reinforcing fibers comprisemetal fibers, metalized inorganic fibers, metallized synthetic fibers,glass fibers, carbon fibers, aramid fibers, ceramic fibers andcombinations thereof. In some embodiments, the prepreg comprises anadhesive layer disposed on the at least one surface comprising therepellent treated reinforcing materials. In certain examples, theadhesive layer comprises a polyolefin adhesive, an ethylene-vinylacetate adhesive, a polyamide adhesive, a polyester adhesive, apolyurethane adhesive, a thermoplastic polyurethane adhesive, a styreneblock copolymer adhesive, a polycarbonate adhesive, a fluoropolymericadhesive, a silicone adhesive, a silicone rubber adhesive, anelastomeric adhesive, or a pyrrole adhesive. In further examples, theprepreg may comprise a substrate disposed on the adhesive layer. In someembodiments, the repellent treated reinforcing materials are effectiveto render the adhesive temperature and/or viscosity insensitive. Inother embodiments, the thermoplastic material of the prepreg comprisespolyethylene, polypropylene, polystyrene, acrylonitrylstyrene,butadiene, polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In certain configurations, the prepreg maycomprise a flame retardant. In some instances, some portion of a surfaceof the prepreg comprises a repellency grade number of at least 3 astested by ISO 23232 dated 2009.

In another aspect, a core comprising a web of open celled structuresdefined by random crossing over of reinforcing materials held togetherby a thermoplastic material, the core comprising a repellent treatmenton a surface of the core, in which the repellent treatment is effectiveto decrease absorption of a fluid into voids of the core is provided.

In certain embodiments, the reinforcing materials comprise reinforcingfibers. In other embodiments, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the core. In some instances, the reinforcing fibers comprise metalfibers, metalized inorganic fibers, metallized synthetic fibers, glassfibers, carbon fibers, aramid fibers, ceramic fibers and combinationsthereof. In further examples, the core may comprise an adhesive layerdisposed on the at least one surface comprising the repellent treatment.In some embodiments, the adhesive layer comprises a polyolefin adhesive,an ethylene-vinyl acetate adhesive, a polyamide adhesive, a polyesteradhesive, a polyurethane adhesive, a thermoplastic polyurethaneadhesive, a styrene block copolymer adhesive, a polycarbonate adhesive,a fluoropolymeric adhesive, a silicone adhesive, a silicone rubberadhesive, an elastomeric adhesive, or a pyrrole adhesive. In someinstances, the core may comprise a substrate disposed on the adhesivelayer. In further examples, the repellent material is effective torender the adhesive temperature insensitive. In certain instances, thethermoplastic material of the core comprises polyethylene,polypropylene, polystyrene, acrylonitrylstyrene, butadiene,polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In further embodiments, the core may comprise aflame retardant. In some instances, some portion of a surface of thecore comprises a repellency grade number of at least 3 as tested by ISO23232 dated 2009.

In another aspect, a core comprising a web of open celled structuresdefined by random crossing over of a plurality of repellent treatedreinforcing materials held together by a thermoplastic material, inwhich the repellent treated reinforcing materials are effective todecrease absorption of a fluid into voids of the core is described.

In certain examples, the reinforcing materials comprise reinforcingfibers. In other examples, the reinforcing fibers are present from about20 weight percent to about 80 weight percent based on the weight of thecore. In some embodiments, the reinforcing fibers comprise metal fibers,metalized inorganic fibers, metallized synthetic fibers, glass fibers,carbon fibers, aramid fibers, ceramic fibers and combinations thereof.In certain instances, the core may comprise an adhesive layer disposedon the at least one surface comprising the repellent treated reinforcingmaterials. In some instances, the adhesive layer comprises a polyolefinadhesive, an ethylene-vinyl acetate adhesive, a polyamide adhesive, apolyester adhesive, a polyurethane adhesive, a thermoplasticpolyurethane adhesive, a styrene block copolymer adhesive, apolycarbonate adhesive, a fluoropolymeric adhesive, a silicone adhesive,a silicone rubber adhesive, an elastomeric adhesive, or a pyrroleadhesive. In certain configurations, a substrate can be disposed on theadhesive layer of the core. In some embodiments, the repellent materialis effective to render the adhesive temperature and/or viscosityinsensitive. In other embodiments, the thermoplastic material of thecore comprises polyethylene, polypropylene, polystyrene,acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, polyvinylchloride, polyphenylene ether, polycarbonates, polyestercarbonates,thermoplastic polyesters, polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In certain examples, the core may comprise a flameretardant. In further examples, some portion of a surface of the corecomprises a repellency grade number of at least 3 as tested by ISO 23232dated 2009.

In an additional aspect, a composite article comprising a prepregcomprising a thermoplastic material and a plurality of reinforcingmaterials dispersed in the thermoplastic material to provide an opencell structure, the prepreg further comprising a repellent treatment onat least one surface of the prepreg, the repellent treatment effectiveto decrease absorption of a fluid into the open cell structure of theprepreg, and a substrate disposed on the prepreg is provided.

In certain embodiments, the reinforcing materials comprise reinforcingfibers. In other embodiments, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the prepreg. In further examples, the reinforcing fibers comprisemetal fibers, metalized inorganic fibers, metallized synthetic fibers,glass fibers, carbon fibers, aramid fibers, ceramic fibers andcombinations thereof. In some instances, the article may comprise anadhesive layer disposed on the at least one surface comprising therepellent treatment. In certain instances, the adhesive layer comprisesa polyolefin adhesive, an ethylene-vinyl acetate adhesive, a polyamideadhesive, a polyester adhesive, a polyurethane adhesive, a thermoplasticpolyurethane adhesive, a styrene block copolymer adhesive, apolycarbonate adhesive, a fluoropolymeric adhesive, a silicone adhesive,a silicone rubber adhesive, an elastomeric adhesive, or a pyrroleadhesive. In some configurations, the substrate comprises a film, afrim, a scrim, a foil, a woven fabric or a non-woven fabric. In otherexamples, the repellent material is effective to render the adhesivetemperature insensitive. In some embodiments, the thermoplastic materialcomprises polyethylene, polypropylene, polystyrene, acrylonitrylstyrene,butadiene, polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some examples, the article may comprise a flameretardant in the prepreg or the substrate or both. In further examples,some portion of a surface of the article, e.g., a surface of theprepreg, comprises a repellency grade number of at least 3 as tested byISO 23232 dated 2009.

In another aspect, a composite article comprising a prepreg comprising athermoplastic material and a plurality of reinforcing materialsdispersed in the thermoplastic material to provide an open cellstructure is provided. In some instances, the composite article may alsocomprise a substrate disposed on the prepreg, the substrate comprising arepellent treatment on at least one surface of the substrate, therepellent treatment effective to decrease absorption of a fluid into thesubstrate, e.g., fluid absorption is less or slower as compared to acomparable surface with no repellent treatment.

In certain examples, the reinforcing materials comprise reinforcingfibers. In some embodiments, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the prepreg. In other embodiments, the reinforcing fibers comprisemetal fibers, metalized inorganic fibers, metallized synthetic fibers,glass fibers, carbon fibers, aramid fibers, ceramic fibers andcombinations thereof. In certain instances, the article may alsocomprise an adhesive layer disposed on the at least one surfacecomprising the repellent treatment. In some embodiments, the adhesivelayer comprises a polyolefin adhesive, an ethylene-vinyl acetateadhesive, a polyamide adhesive, a polyester adhesive, a polyurethaneadhesive, a thermoplastic polyurethane adhesive, a styrene blockcopolymer adhesive, a polycarbonate adhesive, a fluoropolymericadhesive, a silicone adhesive, a silicone rubber adhesive, anelastomeric adhesive, or a pyrrole adhesive. In other instances, thesubstrate comprises a film, a frim, a scrim, a foil, a woven fabric or anon-woven fabric. In further embodiments, the repellent material iseffective to render the adhesive temperature and/or viscosityinsensitive. In additional examples, the thermoplastic material of theprepreg comprises polyethylene, polypropylene, polystyrene,acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, polyvinylchloride, polyphenylene ether, polycarbonates, polyestercarbonates,thermoplastic polyesters, polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some embodiments, the article comprises a flameretardant in the prepreg or the substrate or both. In certain examples,some portion of a surface of the article, e.g., a surface of theprepreg, comprises a repellency grade number of at least 3 as tested byISO 23232 dated 2009.

In an additional aspect, a composite article comprising a prepregcomprising a thermoplastic material and a plurality of repellent treatedreinforcing materials dispersed in the thermoplastic material to providean open cell structure, the repellent treated reinforcing materialseffective to decrease absorption of a fluid into the open cell structureof the prepreg is provided. In certain instances, the article may alsocomprise a substrate disposed on the prepreg.

In certain embodiments, the reinforcing materials comprise reinforcingfibers. In other embodiments, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the prepreg. In additional examples, the reinforcing fibers comprisemetal fibers, metalized inorganic fibers, metallized synthetic fibers,glass fibers, carbon fibers, aramid fibers, ceramic fibers andcombinations thereof. In other examples, the article may comprise anadhesive layer disposed on the at least one surface comprising therepellent treated reinforcing materials. In some instances, the adhesivelayer comprises a polyolefin adhesive, an ethylene-vinyl acetateadhesive, a polyamide adhesive, a polyester adhesive, a polyurethaneadhesive, a thermoplastic polyurethane adhesive, a styrene blockcopolymer adhesive, a polycarbonate adhesive, a fluoropolymericadhesive, a silicone adhesive, a silicone rubber adhesive, anelastomeric adhesive, or a pyrrole adhesive. In certain examples, thesubstrate comprises a film, a frim, a scrim, a foil, a woven fabric or anon-woven fabric. In further embodiments, the repellent material iseffective to render the adhesive temperature and/or viscosityinsensitive. In some examples, the thermoplastic material of the prepregcomprises polyethylene, polypropylene, polystyrene, acrylonitrylstyrene,butadiene, polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In other embodiments, the article may comprise aflame retardant in the prepreg or the substrate or both. In certainexamples, some portion of a surface of the article, e.g., a surface ofthe prepreg, comprises a repellency grade number of at least 3 as testedby ISO 23232 dated 2009.

In another aspect, a composite article comprising a prepreg comprising athermoplastic material and a plurality of repellent treated reinforcingmaterials dispersed in the thermoplastic material to provide an opencell structure, the repellent treated reinforcing materials effective todecrease absorption of a fluid into the open cell structure of theprepreg is provided. In certain instances, the article may also comprisea substrate disposed on the prepreg, the substrate comprising arepellent treatment on at least one surface of the substrate, therepellent treatment effective to decrease absorption of a fluid into thesubstrate.

In some examples, the reinforcing materials comprise reinforcing fibers.In other examples, the reinforcing fibers are present from about 20weight percent to about 80 weight percent based on the weight of theprepreg. In certain embodiments, the reinforcing fibers comprise metalfibers, metalized inorganic fibers, metallized synthetic fibers, glassfibers, carbon fibers, aramid fibers, ceramic fibers and combinationsthereof. In some examples, the article may comprise an adhesive layerdisposed on the at least one surface comprising the repellent treatedreinforcing materials or on at least one repellent treated surface ofthe substrate or both. In certain embodiments, the adhesive layercomprises a polyolefin adhesive, an ethylene-vinyl acetate adhesive, apolyamide adhesive, a polyester adhesive, a polyurethane adhesive, athermoplastic polyurethane adhesive, a styrene block copolymer adhesive,a polycarbonate adhesive, a fluoropolymeric adhesive, a siliconeadhesive, a silicone rubber adhesive, an elastomeric adhesive, or apyrrole adhesive. In other instances,

the substrate comprises a film, a frim, a scrim, a foil, a woven fabricor a non-woven fabric. In further examples, the repellent material iseffective to render the adhesive temperature and/or viscosityinsensitive. In additional embodiments, the thermoplastic material ofthe prepreg comprises polyethylene, polypropylene, polystyrene,acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, polyvinylchloride, polyphenylene ether, polycarbonates, polyestercarbonates,thermoplastic polyesters, polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some examples, the article comprises a flameretardant in the prepreg or the substrate or both.

In certain examples, some portion of a surface of the article, e.g., asurface of the prepreg, comprises a repellency grade number of at least3 as tested by ISO 23232 dated 2009.

In an additional aspect, a composite article comprising a corecomprising a web of open celled structures defined by random crossingover of reinforcing materials held together by a thermoplastic material,the core comprising a repellent treatment on a surface of the core, inwhich the repellent treatment is effective to decrease absorption of afluid into voids of the core is provided. In other examples, the articlemay also comprise a substrate disposed on the core.

In certain examples, the reinforcing materials comprise reinforcingfibers. In other examples, the reinforcing fibers are present from about20 weight percent to about 80 weight percent based on the weight of thecore. In some embodiments, the reinforcing fibers comprise metal fibers,metalized inorganic fibers, metallized synthetic fibers, glass fibers,carbon fibers, aramid fibers, ceramic fibers and combinations thereof.In further examples, the article may comprise an adhesive layer disposedon the at least one surface comprising the repellent treatment. In otherinstances, the adhesive layer comprises a polyolefin adhesive, anethylene-vinyl acetate adhesive, a polyamide adhesive, a polyesteradhesive, a polyurethane adhesive, a thermoplastic polyurethaneadhesive, a styrene block copolymer adhesive, a polycarbonate adhesive,a fluoropolymeric adhesive, a silicone adhesive, a silicone rubberadhesive, an elastomeric adhesive, or a pyrrole adhesive. In furtherexamples, the substrate comprises a film, a frim, a scrim, a foil, awoven fabric or a non-woven fabric. In some embodiments, the repellentmaterial is effective to render the adhesive temperature and/orviscosity insensitive. In some examples, the thermoplastic material ofthe core comprises polyethylene, polypropylene, polystyrene,acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, polyvinylchloride, polyphenylene ether, polycarbonates, polyestercarbonates,thermoplastic polyesters, polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In certain embodiments, the article may comprise aflame retardant in the core or the substrate or both. In certainexamples, some portion of a surface of the article, e.g., a surface ofthe core, comprises a repellency grade number of at least 3 as tested byISO 23232 dated 2009.

In another aspect, a composite article comprising a core comprising aweb of open celled structures defined by random crossing over ofreinforcing materials held together by a thermoplastic material, and asubstrate disposed on the core, the substrate comprising a repellenttreatment on at least one surface of the substrate, and the repellenttreatment effective to decrease absorption of a fluid into the substrateis described.

In certain examples, the reinforcing materials comprise reinforcingfibers. In some embodiments, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the core. In further examples, the reinforcing fibers comprise metalfibers, metalized inorganic fibers, metallized synthetic fibers, glassfibers, carbon fibers, aramid fibers, ceramic fibers and combinationsthereof. In additional examples, the article may comprise an adhesivelayer disposed on the at least one surface comprising the repellenttreatment. In some embodiments, the adhesive layer comprises apolyolefin adhesive, an ethylene-vinyl acetate adhesive, a polyamideadhesive, a polyester adhesive, a polyurethane adhesive, a thermoplasticpolyurethane adhesive, a styrene block copolymer adhesive, apolycarbonate adhesive, a fluoropolymeric adhesive, a silicone adhesive,a silicone rubber adhesive, an elastomeric adhesive, or a pyrroleadhesive. In further examples, the substrate comprises a film, a frim, ascrim, a foil, a woven fabric or a non-woven fabric. In some instances,the repellent material is effective to render the adhesive temperatureand/or viscosity insensitive. In further embodiments, the thermoplasticmaterial of the core comprises polyethylene, polypropylene, polystyrene,acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, polyvinylchloride, polyphenylene ether, polycarbonates, polyestercarbonates,thermoplastic polyesters, polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some examples, the article may comprise a flameretardant in the core or the substrate or both. In certain examples,some portion of a surface of the article, e.g., a surface of the core,comprises a repellency grade number of at least 3 as tested by ISO 23232dated 2009.

In an additional aspect, a composite article comprising a corecomprising a web of open celled structures defined by random crossingover of a plurality of repellent treated reinforcing materials heldtogether by a thermoplastic material, in which the repellent treatedreinforcing materials are effective to decrease absorption of a fluidinto voids of the core is provided. In certain instances, the articlemay also comprise a substrate disposed on the core.

In certain embodiments, the reinforcing materials comprise reinforcingfibers. In certain examples, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the core. In some examples, the reinforcing fibers comprise metalfibers, metalized inorganic fibers, metallized synthetic fibers, glassfibers, carbon fibers, aramid fibers, ceramic fibers and combinationsthereof. In other instances, the article may comprise an adhesive layerdisposed on the at least one surface comprising the repellent treatedreinforcing materials. In further embodiments, the adhesive layercomprises a polyolefin adhesive, an ethylene-vinyl acetate adhesive, apolyamide adhesive, a polyester adhesive, a polyurethane adhesive, athermoplastic polyurethane adhesive, a styrene block copolymer adhesive,a polycarbonate adhesive, a fluoropolymeric adhesive, a siliconeadhesive, a silicone rubber adhesive, an elastomeric adhesive, or apyrrole adhesive. In some examples, the substrate comprises a film, afrim, a scrim, a foil, a woven fabric or a non-woven fabric. In certainembodiments, the repellent material is effective to render the adhesivetemperature and/or viscosity insensitive. In other embodiments, thethermoplastic material of the core comprises polyethylene,polypropylene, polystyrene, acrylonitrylstyrene, butadiene,polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some examples, the article may comprise a flameretardant in the core or the substrate or both. In certain examples,some portion of a surface of the article, e.g., a surface of the core,comprises a repellency grade number of at least 3 as tested by ISO 23232dated 2009.

In another aspect, a composite article comprising a core comprising aweb of open celled structures defined by random crossing over of aplurality of repellent treated reinforcing materials held together by athermoplastic material, in which the repellent treated reinforcingmaterials are effective to decrease absorption of a fluid into voids ofthe core, in which the article also comprises a substrate disposed onthe core, the substrate comprising a repellent treatment on at least onesurface of the substrate, the repellent treatment effective to decreaseabsorption of a fluid into the substrate is disclosed.

In certain embodiments, the reinforcing materials comprise reinforcingfibers. In other embodiments, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the core. In some instances, the reinforcing fibers comprise metalfibers, metalized inorganic fibers, metallized synthetic fibers, glassfibers, carbon fibers, aramid fibers, ceramic fibers and combinationsthereof. In further examples, the article may also comprise an adhesivelayer disposed on the at least one surface comprising the repellenttreated reinforcing materials or on at least one repellent treatedsurface of the substrate or both. In some embodiments, the adhesivelayer comprises a polyolefin adhesive, an ethylene-vinyl acetateadhesive, a polyamide adhesive, a polyester adhesive, a polyurethaneadhesive, a thermoplastic polyurethane adhesive, a styrene blockcopolymer adhesive, a polycarbonate adhesive, a fluoropolymericadhesive, a silicone adhesive, a silicone rubber adhesive, anelastomeric adhesive, or a pyrrole adhesive. In certain instances, thesubstrate comprises a film, a frim, a scrim, a foil, a woven fabric or anon-woven fabric. In other instances, the repellent material iseffective to render the adhesive temperature and/or viscosityinsensitive. In further examples, the thermoplastic material of the corecomprises polyethylene, polypropylene, polystyrene, acrylonitrylstyrene,butadiene, polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some embodiments, the article comprises a flameretardant in the core or the substrate or both. In certain examples,some portion of a surface of the article, e.g., a surface of the core,comprises a repellency grade number of at least 3 as tested by ISO 23232dated 2009.

In an additional aspect, a kit comprising a prepreg or core comprising athermoplastic material and a plurality of reinforcing materialsdispersed in the thermoplastic material to provide an open cellstructure, a repellent material effective to decrease absorption of afluid, e.g., a liquid, adhesive, water or other fluid, into the opencell structure of the prepreg or the core, and instructions fordisposing the repellent material on the prepreg or the core isdescribed.

In certain embodiments, the kit may also comprise a substrate. In otherembodiments, the substrate comprises a film, a frim, a scrim, a foil, awoven fabric or a non-woven fabric. In certain examples, the kit mayalso comprise an adhesive. In other embodiments, the adhesive is apolyolefin adhesive, an ethylene-vinyl acetate adhesive, a polyamideadhesive, a polyester adhesive, a polyurethane adhesive, a thermoplasticpolyurethane adhesive, a styrene block copolymer adhesive, apolycarbonate adhesive, a fluoropolymeric adhesive, a silicone adhesive,a silicone rubber adhesive, an elastomeric adhesive, or a pyrroleadhesive. In some instances, the prepreg or the core of the kit maycomprise at least one surface (or portion thereof) that comprises arepellency grade number of at least 3 as tested by ISO 23232 dated 2009.

In another aspect, a kit comprising a prepreg or core comprising athermoplastic material and a plurality of reinforcing materialsdispersed in the thermoplastic material to provide an open cellstructure, the prepreg or the core further comprising a repellenttreatment on at least one surface of the prepreg or the core, therepellent treatment effective to decrease absorption of a fluid, e.g., aliquid, adhesive, water or other fluid, into the open cell structure ofthe prepreg or the core, aa substrate in the kit, and instructions forusing the substrate with the prepreg or the core to provide an articleis described.

In certain examples, the kit comprises a repellent material to treat thesubstrate. In other examples, the substrate comprises a film, a frim, ascrim, a foil, a woven fabric or a non-woven fabric. In someembodiments, the kit further comprises an adhesive. In other instances,the adhesive is a polyolefin adhesive, an ethylene-vinyl acetateadhesive, a polyamide adhesive, a polyester adhesive, a polyurethaneadhesive, a thermoplastic polyurethane adhesive, a styrene blockcopolymer adhesive, a polycarbonate adhesive, a fluoropolymericadhesive, a silicone adhesive, a silicone rubber adhesive, anelastomeric adhesive, or a pyrrole adhesive. In some instances, theprepreg or the core of the kit may comprise at least one surface (orportion thereof) that comprises a repellency grade number of at least 3as tested by ISO 23232 dated 2009.

In an additional aspect, a kit comprising a thermoplastic material, aplurality of reinforcing materials, a repellent material, andinstructions for producing a prepreg or core using the thermoplasticmaterial, the plurality of reinforcing materials and the repellentmaterial is provided.

In certain embodiments, the kit comprises a substrate. In otherembodiments, the substrate comprises a film, a frim, a scrim, a foil, awoven fabric or a non-woven fabric. In some instances, the kit comprisesan adhesive. In further examples, the adhesive is a polyolefin adhesive,an ethylene-vinyl acetate adhesive, a polyamide adhesive, a polyesteradhesive, a polyurethane adhesive, a thermoplastic polyurethaneadhesive, a styrene block copolymer adhesive, a polycarbonate adhesive,a fluoropolymeric adhesive, a silicone adhesive, a silicone rubberadhesive, an elastomeric adhesive, or a pyrrole adhesive. In someinstances, the instructions provide for producing a prepreg or the corewith at least one surface (or portion thereof) that comprises arepellency grade number of at least 3 as tested by ISO 23232 dated 2009.

In another aspect, a kit comprising a prepreg or core comprising athermoplastic material and a plurality of repellent treated reinforcingmaterials dispersed in the thermoplastic material to provide an opencell structure, the repellent treated reinforcing materials effective todecrease absorption of a fluid, e.g., a liquid, adhesive, water or otherfluid, into the open cell structure of the prepreg, a substrate in thekit, and instructions for coupling the substrate to the prepreg isprovided.

In certain embodiments, the kit comprises a repellent material to treatthe substrate. In other embodiments, the substrate comprises a film, afrim, a scrim, a foil, a woven fabric or a non-woven fabric. In someexamples, the kit comprises an adhesive. In certain examples, theadhesive is a polyolefin adhesive, an ethylene-vinyl acetate adhesive, apolyamide adhesive, a polyester adhesive, a polyurethane adhesive, athermoplastic polyurethane adhesive, a styrene block copolymer adhesive,a polycarbonate adhesive, a fluoropolymeric adhesive, a siliconeadhesive, a silicone rubber adhesive, an elastomeric adhesive, or apyrrole adhesive. In some instances, the prepreg or the core of the kitcomprises at least one surface (or portion thereof) that comprises arepellency grade number of at least 3 as tested by ISO 23232 dated 2009.

In an additional aspect, a method of reducing the weight of a compositearticle, the method comprising treating at least one component of thecomposite article with a repellent material prior to coupling thetreated component to another component of the composite article isprovided.

In certain embodiments, the treated component is configured as a prepregor a core or is configured as a substrate to be coupled to a prepreg orcore. In some examples, the method comprises selecting the repellentmaterial to promote adhesive bead formation on a surface of the treatedcomponent. In other embodiments, the basis weight of the treatedcomponent is less than the basis weight of a non-treated component whilestill providing the same adhesion strength between the treated componentand the another component. In some instances, the basis weight of thetreated component is reduced by at least 20% when the repellenttreatment is used. In certain instances, the treated component comprisesleast one surface (or portion thereof) that comprises a repellency gradenumber of at least 3 as tested by ISO 23232 dated 2009.

In another aspect, a method of reducing the amount of adhesive used tocouple components of a composite article, the method comprising treatinga surface of a component of the composite article, prior to formation ofthe composite article, with a repellent material that is effective todecrease absorption of a fluid, e.g., a liquid, adhesive, water or otherfluid, into the component is provided.

In certain embodiments, the method comprises configuring the surface tobe treated as a surface of a prepreg or core or a surface of asubstrate. In other embodiments, the method comprises disposing anadhesive on the treated surface. In further embodiments, the methodcomprises selecting the repellent material to permit at least 20% lessadhesive by weight to be used to couple the components and provide thesame adhesion strength between components as present when no repellentmaterial is used. In certain examples, the method comprises disposing aneffective amount of the repellent material on the surface to promoteadhesive bead formation on the surface after deposition of an adhesiveon the treated surface. In some instances, the treated surface (orportion thereof) comprises a repellency grade number of at least 3 astested by ISO 23232 dated 2009.

In an additional aspect, a kit for assembling a shower stall comprisingat least one prepreg as described herein and instructions for using theprepreg to install the shower stall is provided. In certain instances,the reinforcing materials of the prepreg comprise reinforcing fibers. Inother instances, the reinforcing fibers comprise metal fibers, metalizedinorganic fibers, metallized synthetic fibers, glass fibers, carbonfibers, aramid fibers, ceramic fibers and combinations thereof. In someembodiments, the kit comprises at least one surface finishing materialselected from an acrylic panel and tiling. In additional embodiments,the kit comprises an adhesive configured to be disposed on a surface ofthe prepreg between the prepreg and the surface finishing material. Inother embodiments, the adhesive comprises a polyolefin adhesive, anethylene-vinyl acetate adhesive, a polyamide adhesive, a polyesteradhesive, a polyurethane adhesive, a thermoplastic polyurethaneadhesive, a styrene block copolymer adhesive, a polycarbonate adhesive,a fluoropolymeric adhesive, a silicone adhesive, a silicone rubberadhesive, an elastomeric adhesive, or a pyrrole adhesive. In someinstances, the repellent material is effective to render the adhesivetemperature insensitive. In other instances, the thermoplastic materialcomprises polyethylene, polypropylene, polystyrene, acrylonitrylstyrene,butadiene, polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some instances, the kit comprises a pluralityof prepregs, each comprising a prepreg as described herein, in whicheach prepreg is sized and arranged to cover one surface of a wallstructure configured to receive a shower panel. In some embodiments, thekit comprises a plurality of shower panels. In some instances, theprepreg surface (or portion thereof) comprises a repellency grade numberof at least 3 as tested by ISO 23232 dated 2009.

In another aspect, a kit for assembling a shower stall comprising atleast one core of and instructions for using the core to install theshower stall is provided. In certain embodiments, the reinforcingmaterials of the core comprise reinforcing fibers. In other embodiments,the reinforcing fibers comprise metal fibers, metalized inorganicfibers, metallized synthetic fibers, glass fibers, carbon fibers, aramidfibers, ceramic fibers and combinations thereof. In some instances, thekit comprises at least one surface finishing material selected from anacrylic panel and tiling. In other instances, the kit comprises anadhesive configured to be disposed on a surface of the core between thecore and the surface finishing material. In further examples, theadhesive comprises a polyolefin adhesive, an ethylene-vinyl acetateadhesive, a polyamide adhesive, a polyester adhesive, a polyurethaneadhesive, a thermoplastic polyurethane adhesive, a styrene blockcopolymer adhesive, a polycarbonate adhesive, a fluoropolymericadhesive, a silicone adhesive, a silicone rubber adhesive, anelastomeric adhesive, or a pyrrole adhesive. In some embodiments, therepellent material is effective to render the adhesive temperatureinsensitive. In other embodiments, the thermoplastic material comprisespolyethylene, polypropylene, polystyrene, acrylonitrylstyrene,butadiene, polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some instances, the kit comprises a pluralityof cores, each comprising the core of claim 21 or the core of claim 31,in which each prepreg is sized and arranged to cover one surface of awall structure configured to receive a shower panel. In certaininstances, the kit comprises a plurality of shower panels. In someembodiments, the kit comprises a plurality of shower panels. In someinstances, the prepreg surface (or portion thereof) comprises arepellency grade number of at least 3 as tested by ISO 23232 dated 2009.

In another aspect, a kit for assembling a shower stall comprising atleast one composite article described herein and instructions for usingthe article to install the shower stall is provided. In some instances,a surface (or portion thereof) of the article comprises a repellencygrade number of at least 3 as tested by ISO 23232 dated 2009.

In an additional aspect, a kit for finishing an interior surface of abuilding, the kit comprising one of the prepregs described herein, oneof the cores described herein, or one of the composite articlesdescribed herein is provided. In some instances, a surface (or portionthereof) of the prepreg, core or article comprises a repellency gradenumber of at least 3 as tested by ISO 23232 dated 2009.

In another aspect, a method of deterring mold growth in a buildingstructure, the method comprising installing at least one prepreg asdescribed herein on an interior surface of the building structure isprovided. In some instances, a surface (or portion thereof) of theprepreg comprises a repellency grade number of at least 3 as tested byISO 23232 dated 2009.

In another aspect, a method of deterring mold growth in a buildingstructure, the method comprising installing at least one core asdescribed herein on an interior surface of the building structure isprovided. In some instances, a surface (or portion thereof) of the corecomprises a repellency grade number of at least 3 as tested by ISO 23232dated 2009.

In an additional aspect, a method of deterring mold growth in a buildingstructure, the method comprising installing at least one compositearticle as described herein on an interior surface of the buildingstructure is provided. In some instances, a surface (or portion thereof)of the article comprises a repellency grade number of at least 3 astested by ISO 23232 dated 2009.

In another aspect, a method of facilitating production of an antifungalsurface, the method comprising providing one of the prepregs asdescribed herein and providing instructions for using the prepreg toprovide the antifungal surface is disclosed. In some instances, asurface (or portion thereof) of the prepreg comprises a repellency gradenumber of at least 3 as tested by ISO 23232 dated 2009.

In another aspect, a method of facilitating production of an antifungalsurface, the method comprising providing one of the cores as describedherein and providing instructions for using the core to provide theantifungal surface is disclosed. In some instances, a surface (orportion thereof) of the core comprises a repellency grade number of atleast 3 as tested by ISO 23232 dated 2009.

In another aspect, a method of facilitating production of an antifungalsurface, the method comprising providing one of the composite articlesas described herein and providing instructions for using the article toprovide the antifungal surface is disclosed. In some instances, asurface (or portion thereof) of the article comprises a repellency gradenumber of at least 3 as tested by ISO 23232 dated 2009.

In an additional aspect, a prepreg comprising a thermoplastic materialand a plurality of reinforcing materials dispersed in the thermoplasticmaterial to provide an open cell structure, the prepreg furthercomprising a repellent treatment on at least one surface of the prepreg,the repellent treatment effective to decrease absorption of a fluid intothe open cell structure of the prepreg, in which some portion of asurface of the prepreg comprises a repellency grade number of at least 3as tested by ISO 23232 dated 2009 is provided.

In certain embodiments, the reinforcing materials comprise reinforcingfibers. In other embodiments, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the prepreg. In some examples, the reinforcing fibers comprise metalfibers, metalized inorganic fibers, metallized synthetic fibers, glassfibers, carbon fibers, aramid fibers, ceramic fibers and combinationsthereof. In certain embodiments, the prepreg may comprise an adhesivelayer disposed on the at least one surface comprising the repellenttreatment. In other instances, the adhesive layer comprises a polyolefinadhesive, an ethylene-vinyl acetate adhesive, a polyamide adhesive, apolyester adhesive, a polyurethane adhesive, a thermoplasticpolyurethane adhesive, a styrene block copolymer adhesive, apolycarbonate adhesive, a fluoropolymeric adhesive, a silicone adhesive,a silicone rubber adhesive, an elastomeric adhesive, or a pyrroleadhesive. In certain examples, the prepreg may comprise a substratedisposed on the adhesive layer. In other embodiments, the repellentmaterial is effective to render the adhesive temperature insensitive. Infurther embodiments, the thermoplastic material of the prepreg comprisespolyethylene, polypropylene, polystyrene, acrylonitrylstyrene,butadiene, polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some instances, the prepreg may comprise aflame retardant.

In another aspect, a prepreg comprising a thermoplastic material and aplurality of repellent treated reinforcing materials dispersed in thethermoplastic material to provide an open cell structure, the repellenttreated reinforcing materials effective to decrease absorption of afluid into the open cell structure of the prepreg, in which some portionof a surface of the prepreg comprises a repellency grade number of atleast 3 as tested by ISO 23232 dated 2009 is disclosed.

In certain embodiments, the reinforcing materials comprise reinforcingfibers. In certain examples, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the prepreg. In other examples, the reinforcing fibers comprise metalfibers, metalized inorganic fibers, metallized synthetic fibers, glassfibers, carbon fibers, aramid fibers, ceramic fibers and combinationsthereof. In certain embodiments, the prepreg may further comprise anadhesive layer disposed on the at least one surface comprising therepellent treated reinforcing materials. In other embodiments, theadhesive layer comprises a polyolefin adhesive, an ethylene-vinylacetate adhesive, a polyamide adhesive, a polyester adhesive, apolyurethane adhesive, a thermoplastic polyurethane adhesive, a styreneblock copolymer adhesive, a polycarbonate adhesive, a fluoropolymericadhesive, a silicone adhesive, a silicone rubber adhesive, anelastomeric adhesive, or a pyrrole adhesive. In certain instances, theprepreg further comprises a substrate disposed on the adhesive layer. Inother examples, the repellent treated reinforcing materials areeffective to render the adhesive temperature and/or viscosityinsensitive. In some examples, the thermoplastic material comprisespolyethylene, polypropylene, polystyrene, acrylonitrylstyrene,butadiene, polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In certain instances, the prepreg comprises aflame retardant.

In an additional aspect, a core comprising a web of open celledstructures defined by random crossing over of reinforcing materials heldtogether by a thermoplastic material, the core comprising a repellenttreatment on a surface of the core, in which the repellent treatment iseffective to decrease absorption of a fluid into voids of the core, inwhich some portion of a surface of the core comprises a repellency gradenumber of at least 3 as tested by ISO 23232 dated 2009 is provided.

In certain examples, the reinforcing materials comprise reinforcingfibers. In other examples, the reinforcing fibers are present from about20 weight percent to about 80 weight percent based on the weight of thecore. In further embodiments, the reinforcing fibers comprise metalfibers, metalized inorganic fibers, metallized synthetic fibers, glassfibers, carbon fibers, aramid fibers, ceramic fibers and combinationsthereof. In some examples, the core may comprise an adhesive layerdisposed on the at least one surface comprising the repellent treatment.In other examples, the adhesive layer comprises a polyolefin adhesive,an ethylene-vinyl acetate adhesive, a polyamide adhesive, a polyesteradhesive, a polyurethane adhesive, a thermoplastic polyurethaneadhesive, a styrene block copolymer adhesive, a polycarbonate adhesive,a fluoropolymeric adhesive, a silicone adhesive, a silicone rubberadhesive, an elastomeric adhesive, or a pyrrole adhesive. In certaininstances, the core may comprise a substrate disposed on the adhesivelayer. In other instances, the repellent material is effective to renderthe adhesive temperature insensitive. In further examples, thethermoplastic material comprises polyethylene, polypropylene,polystyrene, acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, polyvinylchloride, polyphenylene ether, polycarbonates, polyestercarbonates,thermoplastic polyesters, polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some embodiments, the core may include a flameretardant.

In another aspect, a core comprising a web of open celled structuresdefined by random crossing over of a plurality of repellent treatedreinforcing materials held together by a thermoplastic material, inwhich the repellent treated reinforcing materials are effective todecrease absorption of a fluid into voids of the core, in which someportion of a surface of the core comprises a repellency grade number ofat least 3 as tested by ISO 23232 dated 2009 is described.

In certain embodiments, the reinforcing materials comprise reinforcingfibers. In other embodiments, the reinforcing fibers are present fromabout 20 weight percent to about 80 weight percent based on the weightof the core. In additional examples, the reinforcing fibers comprisemetal fibers, metalized inorganic fibers, metallized synthetic fibers,glass fibers, carbon fibers, aramid fibers, ceramic fibers andcombinations thereof. In certain examples, the core may comprise anadhesive layer disposed on the at least one surface comprising therepellent treated reinforcing materials. In some instances, the adhesivelayer comprises a polyolefin adhesive, an ethylene-vinyl acetateadhesive, a polyamide adhesive, a polyester adhesive, a polyurethaneadhesive, a thermoplastic polyurethane adhesive, a styrene blockcopolymer adhesive, a polycarbonate adhesive, a fluoropolymericadhesive, a silicone adhesive, a silicone rubber adhesive, anelastomeric adhesive, or a pyrrole adhesive. In other embodiments, thecore may comprise a substrate disposed on the adhesive layer. In someembodiments, the repellent material is effective to render the adhesivetemperature and/or viscosity insensitive. In certain instances, thethermoplastic material comprises polyethylene, polypropylene,polystyrene, acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, polyvinylchloride, polyphenylene ether, polycarbonates, polyestercarbonates,thermoplastic polyesters, polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof. In some examples, the core may comprise a flameretardant.

Additional aspects, examples, embodiments and features are described inmore detail below.

BRIEF DESCRIPTION OF THE FIGURES

Certain features, aspect and components of illustrative configurationsare described in more detail below in which:

FIG. 1 is an illustration of an article comprising a substrate coupledto a prepreg or core using a repellent material and optionally anadhesive, in accordance with certain configurations;

FIG. 2A is an illustration of an article comprising a prepreg or coreand a substrate comprising a repellent material and optionally anadhesive, in accordance with certain configurations;

FIG. 2B is an illustration of an article comprising a prepreg or coreand a substrate comprising a repellent material and optionally anadhesive and further including a second substrate disposed on thesubstrate, in accordance with certain configurations;

FIG. 3A is an illustration of an article comprising two prepreg or corelayers coupled to each other using a repellent material, in accordancewith certain configurations;

FIG. 3B is an illustration of an article comprising two prepreg or corelayers coupled to each other using a repellent material and an adhesive,in accordance with certain configurations;

FIG. 4 is an illustration of an article comprising two or moresubstrates, in accordance with certain configurations;

FIG. 5 is an illustration of an article comprising a substrate on morethan one surface of a prepreg or core layer, in accordance with certainconfigurations;

FIG. 6A is an illustration of an article comprising a prepreg or coreand a substrate comprising, on a least two surfaces, a repellentmaterial and optionally an adhesive, in accordance with certainconfigurations;

FIG. 6B is an illustration of an article comprising a prepreg or coreand, on each surface, a substrate comprising a repellent material andoptionally an adhesive and further including a second substrate disposedon one of the other substrates, in accordance with certainconfigurations;

FIG. 7 is an illustration of an article comprising a plurality ofprepreg or core layers and a plurality of substrate layers, inaccordance with certain configurations;

FIG. 8 is an illustration of an article comprising a prepreg and aplurality of substrates, in accordance with certain configurations;

FIG. 9 is an illustration of two substrates coupled to each otherthrough a repellent layer, in accordance with certain examples;

FIG. 10 is a photograph showing four different drop shapes (A-D) inaccordance with certain examples;

FIG. 11 is an illustration of a house comprising roof underlaymentpanels, in accordance with certain configurations;

FIG. 12 is an illustration of a shower stall, in accordance with certainexamples;

FIG. 13 is an illustration of some components which can be used inbuilding applications, in accordance with certain examples;

FIGS. 14A and 14B are photographs of boards treated with a repellent todemonstrate adhesive bead formation, in accordance with certainconfigurations;

FIGS. 15A and 15B are microscope images of the boards of FIGS. 14A and14B showing adhesive bead formation on repellent treated boards, inaccordance with certain configurations;

FIGS. 16A and 16B are photographs of boards treated with a repellent todemonstrate adhesive bead formation, in accordance with certainconfigurations;

FIGS. 17A and 17B are microscope images of the boards of FIGS. 16A and16B showing adhesive bead formation on repellent treated boards, inaccordance with certain configurations;

FIGS. 18A and 18B are photographs of boards treated with a repellent todemonstrate adhesive bead formation, in accordance with certainconfigurations;

FIGS. 19A and 19B are microscope images of the boards of FIGS. 18A and18B showing an adhesive coating on repellent treated boards, inaccordance with certain configurations;

FIGS. 20A and 20B are photographs of boards treated with a repellent todemonstrate adhesive bead formation, in accordance with certainconfigurations;

FIGS. 21A and 21B are microscope images of the boards of FIGS. 20A and20B showing adhesive bead formation on repellent treated boards, inaccordance with certain configurations; and

FIGS. 22A and 22B are microscope images showing free and constrainedexpansion of urethane coated boards, in accordance with certainconfigurations;

The particular dimensions, thicknesses and arrangement of the componentsof the figures are provided for illustration purposes. Unless otherwisespecified, the thickness of one component, relative to the thickness ofanother component, may be varied as desired. Where materials aredescribed as being present on a surface, the material may be presentacross the entire surface or only a portion thereof.

DETAILED DESCRIPTION

Certain embodiments, examples, and configurations are described below toillustrate better some of the many attributes, advancements and featuresof the technology. Reference to the terms “top,” “bottom” or “side” isprovided for convenience purposes only and not intended to limit aparticular surface, or portion thereof, where two or more components maybe coupled to each other. The term “layer” is referred to below incertain instances for illustration purposes. Where a material is statedto be present in a “layer,” the material may instead be coated onindividual materials or portions thereof instead of being a solid orcontinuous layer across a surface of a component. The term “fluid” isused herein in certain instances and is intended to refer to liquids,oils, gases, and materials in the form of a liquid or flowablesemi-solid, e.g., liquid adhesives including water based adhesives, oilbased adhesives and the like.

In certain configurations of the prepregs, cores, substrates andarticles described herein, one or more components may be coated ortreated with a repelling agent also referred to herein in certaininstances as a repellent. While not wishing to be bound by anyparticular scientific theory, the repelling agent may generally beeffective to promote decreased fluid absorption rates into a substrate,or component thereof. For example, in a typical porous thermoplasticcomposite material, liquid adhesive disposed on the surface may be drawninto the porous interior quickly reducing the amount present on thesurface for coupling another component. In certain embodiments of thearticles and components thereof described herein, one or more componentsmay be treated with a repellent to promote retention of the fluid, e.g.,adhesive, on a bonding surface of a substrate to enhance bonding toanother substrate or component. In some examples, the enhanced retentionof the adhesive on a bonding substrate permits the use of less adhesivefor a desired bonding strength, permits the use of lighter materialswhile providing a similarly desired peel strength or may permit the useof adhesives, e.g., less viscous adhesives such as liquid adhesives,that otherwise may not be useable due to fast absorption into theinterior of the substrate.

In certain embodiments, the repellents and repellent coatings describedherein can be selected from suitable compounds and materials that canpromote fluid bead formation on a surface of a material. For example, inthe absence of the repellent material, when a fluid is added to an opencell or porous substrate, a substantial amount of the fluid is drawninto the interior void space by way of capillary action. By including arepellent material, the fluid may form beads on the surface andgenerally be retained on the surface to a more substantial degree thanwhen no repellent material is present on the material. Illustrativerepellent compounds and materials include, but are not limited to,compounds comprising silicon (Si) such as, for example, siloxanes,polysiloxanes, silanes and organosilanes, compounds comprising perfluorogroups (e.g., a perfluoroether or a perfluoropolymer), fluoropolymerssuch as polytetrafluoroethylene, arsenates, and other materials whichare effective to promote reduced absorption of adhesives into theinterior of a substrate. While the repellent material may provide forenhanced retention of fluid on a surface, it can be desirable to permitsome fluid, e.g., some adhesive, to be absorbed into the substrate toprovide an anchoring effect between the substrate and another component.By permitting some penetration of liquid adhesive but providing enhancedamounts on the surface, delamination of components can be greatlyreduced.

In some embodiments, where a liquid adhesive is used with a repellentmaterial, the repellent may be used in an effective amount to permit atleast 20% or 25% less adhesive (by weight) to be present between twocomponents to provide the same or greater adhesion strength. Forexample, where a polyethyleneterephthalate substrate is coupled to afiber bearing polypropylene core, the coupling of the two componentsprovides a certain adhesion strength between them. The addition of arepellent material to the substrate or the core can permit the use of atleast 20% or 25% or less adhesive by weight to provide the same adhesionstrength as when no repellent material is present but where increasedamounts of adhesive are required. In some examples, the presence of arepellent treatment on the substrate may permit the use of at least 30%less adhesive by weight, 35% less adhesive by weight, 40% less adhesiveby weight, 45% less adhesive by weight or even less than 50% by weightadhesive to provide the same adhesion or bonding strength provided whenincreased amounts of adhesive are used but where no repellent treatmentis present.

In certain configurations, the presence of a repellent treatment maypermit lighter weight substrates to be used, which can reduce theoverall cost of the article. For example, the enhanced adhesion strengthpermits the use of thinner materials, e.g., thinner scrims or othersubstrates, while still providing the desired aesthetic and performancecharacteristics. In some embodiments, the basis weight of the substratethat is coupled to a prepreg or core (as described in more detail below)may be reduced by at least 20%, 25% or 30% as compared with the weightof a substrate needed to provide the same performance characteristics,e.g., adhesion strength, resistance to delamination, etc. where norepellent material is present. It is an unexpected result that, when arepellent material is present, a lower basis weight substrate can bepresent in an article even where lesser amounts of adhesive are presentand the performance characteristics are the same or better as when thebasis weight of the substrate is more and the amount of adhesive used ismore but where no repellent material is present. In certain instances,the basis weight of the substrate may be about 10 grams per square meter(gsm), 15 gsm, 20, gsm, 25 gsm, 30 gsm or any value in between thesevalues while still providing suitable performance characteristics.Substrates with basis weights greater than 30 gsm may also be used ifdesired though heavier articles will be produced when heavier substratesare present. As noted below, the overall basis weight of the article maybe reduced, while still retaining desired properties, when a repellentmaterial is present as compared to a similar article that lacks arepellent but has the same desired properties.

In some instances, the repellent material is effective to render thefluid temperature insensitive and/or viscosity insensitive. For example,in many instances, a liquid adhesive must be selected based on a desiredcure time which varies with ambient temperature in the processingenvironment. In colder temperatures, a faster cure adhesive may beneeded to provide suitable adhesion strength. In warmer temperatures, aslower curing adhesive may be used. In embodiments described herein,enhanced retention of the adhesive on the surface by the presence of arepellent material generally renders the adhesive suitable for use overa much broader ambient temperature range, e.g., 0 degrees Celsius up to40 degrees Celsius. By using a repellent material, for example, a singleliquid adhesive can be used over a much broader temperature range.Similarly, as the repellent material is selected to reduce absorption offluid into the core (or the substrate or both), the viscosity of thefluid generally does not matter when it comes to performing one or moreprocessing operations using the fluid.

In certain embodiments, the prepregs, cores, composites and articlesdescribed herein may comprise two or more different components which canbe coupled to each other, at least in part, using one or more fluids,e.g., liquid adhesives that are water based adhesives or oil basedadhesives. In some embodiments, a prepreg comprising one or morethermoplastic materials and comprising a surface coating can be used.For example, the prepreg may comprise one or more thermoplasticmaterials in combination with one or more other materials, e.g., afiller, an additive, a flame retardant, a smoke suppressant, loftingagents, a strengthening agent, powders, particles, biocidal agents,fibers, whiskers, nanomaterials, nanostructures, nanofibers or othermaterials that can impart desired physical or chemical properties to theprepreg. In some embodiments, the prepreg is a substantially porousstructure comprising open cell structures formed by processing of thethermoplastic material and/or other materials used with thethermoplastic material. The open cell structure provides a generallyporous or permeable structure which reduces the overall weight of thecore. For example, the void content of prepreg, prior to processing, mayrange in general between about 5% and about 95% and in particularbetween about 30% and about 80% of the total volume of prepreg. Inanother embodiment, a porous prepreg can be made up of open cellstructures formed by random crossing over of reinforcing materials heldtogether, at least in part, by one or more thermoplastic materials,where about 5% to about 100% of the cell structure are open and allowthe flow of air and gases through. In certain instances, the open cellstructure can be designed to permit passage or air or gases whilehindering, to at least some degree, the passage of a fluid. As notedherein, addition of a repellent material can further inhibit absorptionof fluid into the open cell structure. In some instances, the prepregcomprises a density of about 0.1 gm/cc to about 2.0 gm/cc and in anotherembodiment about 0.3 gm/cc to about 1.0 gm/cc. The exact process used toform the prepreg may vary, and illustrative processes include, but arenot limited to, a wet laid process, an air laid process, a dry blendprocess, a carding and needle process, and other known process that areemployed for making non-woven products. Combinations of suchmanufacturing processes are also useful. In preparing the prepreg, thethermoplastic material can be heated above the glass transitiontemperature of the thermoplastic material to substantially soften theplastic materials. The softened material can be passed through one ormore consolidation devices, for example nip rollers, calendaring rolls,double belt laminators, indexing presses, multiple daylight presses,autoclaves, and other such devices used for lamination and consolidationof sheets and fabrics so that the plastic material can flow. The gapbetween the consolidating elements in the consolidation devices are setto a dimension less than that of the unconsolidated web and greater thanthat of the web if it were to be fully consolidated, thus allowing theprepreg to expand and remain substantially permeable after passingthrough the rollers. In one embodiment, the gap is set to a dimensionabout 5% to about 10% greater than that of the prepreg if it were to befully consolidated. A fully consolidated prepreg is fully compressed andsubstantially void free. A fully consolidated prepreg would have lessthan 5% void content and have negligible open cell structure. Inembodiments described herein, the porosity or void content of theprepreg may be desirably greater than 50%, based on the total volume ofthe prepreg, as the presence of a repellent, even where high porositiesare present, reduces absorption of fluids by the prepreg. As notedherein, the prepreg may be further processed to provide a core layer, acomposite material or an article.

In certain configurations, the thermoplastic material of the prepreg maycomprise, at least in part, one or more of polyethylene, polypropylene,polystyrene, acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, and polyvinylchloride, both plasticized and unplasticized, and blends of thesematerials with each other or other polymeric materials. Other suitablethermoplastics include, but are not limited to, polyarylene ethers,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyetherimides, polyamides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, liquid crystalline polymers, poly(1,4 phenylene)compounds commercially known as PARMAX®, high heat polycarbonate such asBayer's APEC® PC, high temperature nylon, and silicones, as well asalloys and blends of these materials with each other or other polymericmaterials. The thermoplastic material used to form the prepreg can beused in powder form, resin form, rosin form, fiber form or othersuitable forms.

In some instances, once the prepreg is formed, but prior to curing orfurther processing, a repellent may be disposed on or otherwise added toone or more surfaces of the prepreg. For example, the prepreg may bedipped into the repellent, or repellent may be sprayed, coated, rolled,brushed or otherwise disposed on one or more surfaces of the prepreg.The exact amount of repellent disposed on the prepreg may depend, forexample, on the adhesive to be used, the desired bonding strength toanother component, processing temperatures or other considerations. Insome instances, the repellent is disposed to provide a generallycontinuous coating over a surface, whereas in other instances therepellent may be disposed only in certain areas. In some instances,enough repellent is disposed such that 25% or less (by weight or byvolume as desired) adhesive can be used to adhere a substrate to theprepreg at a selected bonding strength as compared to the amount ofadhesive needed to provide the same bonding strength when no repellentis present. In other configurations, enough repellent is disposed suchthat 50% or less (by weight or by volume as desired) adhesive can beused to adhere a substrate to the prepreg at a selected bonding strengthas compared to the amount of adhesive needed to provide the same bondingstrength when no repellent is present. In other examples, enoughrepellent is disposed such that 60%, 65%, 70%, 75% or 80% or less (byweight or by volume as desired) adhesive can be used to adhere asubstrate to the prepreg at a selected bonding strength as compared tothe amount of adhesive needed to provide the same bonding strength whenno repellent is present. In certain embodiments, the repellent may becured or dried on the prepreg prior to disposal of any adhesive orsubstrate on the prepreg. In other instances, the repellent can bedisposed on the prepreg subsequent to prepreg formation, and an adhesive(or other fluid) can be disposed on the prepreg prior to any curing ordrying of the repellent. In some embodiments, an adhesive can beco-added with a repellent agent, e.g., by co-spraying or co-coating, toincrease the rate at which material can be produced.

In some examples, once the repellent is added to the prepreg or asurface thereof, a suitable amount of an adhesive material, which maycomprise any one or more adhesives described herein or other suitablematerials which can provide some adherence, is then added followed byplacement of another substrate on the adhesive bearing prepreg. As notedherein, the additional substrate may take many forms including, but notlimited to, scrims (woven or nonwoven), films, frims (woven ornon-woven), fabrics (woven or non-woven) and other substrate materialsas described herein. The adhesive may be permitted to cure, e.g., usingheat, drying, molding, pressure, light, cross-linkers or other physicalor chemical means to couple the substrate (to at least some degree) tothe prepreg. The presence of the repellent on the prepreg can promotebead formation of the liquid adhesive on the prepreg surface as noted inmore detail below. Bead formation generally can increase the surfacelevel of adhesive and promote better adhesion between the substrate andthe prepreg. While it may be desirable to promote bead formation, it canalso be desirable to permit a certain level of adhesive to enter intothe porous prepreg to anchor the adhesive in the core. In addition, theprepreg itself may provide some adherence to the substrate. Thecombination of added adhesive with the adhesive nature of a repellentcoated prepreg can provide increased bonding strength to the substrate.Depending on the desired level of adherence between the substrate andthe prepreg, different amounts of repellent can be added to promote moreadherence or favor less adherence.

In some examples, the repellent can be used to provide an article thatmay be a composite article that includes a porous or permeable corecoupled to one or more additional substrates or layers. In someembodiments, the porous core may comprise one or more thermoplasticmaterials and can be the cured or processed form of the prepregsdescribed herein. For example, the porous core may comprise one or morethermoplastic materials in combination with a filler, an additive, aflame retardant, a smoke suppressant, a strengthening agent, loftingagents, powders, particles, biocidal agents, fibers, whiskers,nanomaterials, nanostructures, nanofibers or other materials that canimpart desired physical or chemical properties to the core. In someembodiments, the core comprises a web made up of open cell structuresformed by random crossing over of reinforcing materials held together,at least in part, by one or more thermoplastic materials. The webprovides a generally porous structure which reduces overall weight ofthe core. For example, the void content of core ranges in generalbetween about 5% and about 95% and in particular between about 30% andabout 80% of the total volume of core. In an another embodiment, aporous core can be made up of open cell structures formed by randomcrossing over of reinforcing materials held together, at least in part,by one or more thermoplastic materials, where about 40% to about 100% ofthe cell structure are open and allow the flow of air and gases through.In some instances, the core comprises a density of about 0.1 gm/cc toabout 2.0 gm/cc and in another embodiment about 0.3 gm/cc to about 1.0gm/cc. The exact process used to form the core may vary, andillustrative processes include, but are not limited to, a wet laidprocess, an air laid process, a dry blend process, a carding and needleprocess, and other known process that are employed for making non-wovenproducts. Combinations of such manufacturing processes are also useful.In preparing the core, the web comprising the thermoplastic material canbe heated above the glass transition temperature of the thermoplasticmaterial to substantially soften the plastic materials. The softenedmaterial can be passed through one or more consolidation devices, forexample nip rollers, calendaring rolls, double belt laminators, indexingpresses, multiple daylight presses, autoclaves, and other such devicesused for lamination and consolidation of sheets and fabrics so that theplastic material can flow. The gap between the consolidating elements inthe consolidation devices are set to a dimension less than that of theunconsolidated web and greater than that of the web if it were to befully consolidated, thus allowing the web to expand and remainsubstantially permeable after passing through the rollers. In oneembodiment, the gap is set to a dimension about 5% to about 10% greaterthan that of the web if it were to be fully consolidated. A fullyconsolidated web means a web that is fully compressed and substantiallyvoid free. A fully consolidated web would have less than 5% void contentand have negligible open cell structure. In embodiments describedherein, the porosity or void content of the core may be desirablygreater than 50%, based on the total volume of the core, as the presenceof a repellent, even where high porosities are present, reducesabsorption of adhesive by the core.

In certain configurations, the thermoplastic material of the core maycomprise, at least in part, one or more of polyethylene, polypropylene,polystyrene, acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, and polyvinylchloride, both plasticized and unplasticized, and blends of thesematerials with each other or other polymeric materials. Other suitablethermoplastics include, but are not limited to, polyarylene ethers,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyetherimides, polyamides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, liquid crystalline polymers, poly(1,4 phenylene)compounds commercially known as PARMAX®, high heat polycarbonate such asBayer's APEC® PC, high temperature nylon, and silicones, as well asalloys and blends of these materials with each other or other polymericmaterials. The thermoplastic material used to form the web of thecomposite article can be used in powder form, resin form, rosin form,fiber form or other suitable forms. Illustrative thermoplastic materialsin various forms are described herein and are also described, forexample in U.S. Publication Nos. 20130244528 and US20120065283.

In some instances, once the core is formed, a repellent may be disposedon or otherwise added to one or more surfaces of the core. For example,the core may be dipped into the repellent, or repellent may be sprayed,coated, rolled, brushed or otherwise disposed on one or more surfaces ofthe core. The exact amount of repellent disposed on the core may depend,for example, on the adhesive to be used, the desired bonding strength toanother component, processing temperatures or other considerations. Insome instances, the repellent is disposed to provide a generallycontinuous coating over a surface, whereas in other instances therepellent may be disposed only in certain areas. In some instances,enough repellent is disposed such that 25% or less (by weight or byvolume as desired) adhesive can be used to adhere a substrate to thecore at a selected bonding strength as compared to the amount ofadhesive needed to provide the same bonding strength when no repellentis present. In other configurations, enough repellent is disposed suchthat 50% or less (by weight or by volume as desired) adhesive can beused to adhere a substrate to the core at a selected bonding strength ascompared to the amount of adhesive needed to provide the same bondingstrength when no repellent is present. In other examples, enoughrepellent is disposed such that 60%, 65%, 70%, 75% or 80% or less (byweight or by volume as desired) adhesive can be used to adhere asubstrate to the core at a selected bonding strength as compared to theamount of adhesive needed to provide the same bonding strength when norepellent is present. In certain embodiments, the repellent may be curedor dried on the core prior to disposal of any adhesive on the core. Inother instances, the repellent can be disposed on the core subsequent tocore formation, and an adhesive can be disposed on the core prior to anycuring or drying of the repellent. In some embodiments, an adhesive canbe co-added with a repellent agent, e.g., by co-spraying or co-coating,to increase the rate at which material can be produced.

In some examples, once the repellent is added to the core or a surfacethereof, a suitable amount of an adhesive material, which may compriseany one or more adhesives described herein or other suitable materialswhich can provide some adherence, is then added followed by placement ofanother substrate on the adhesive bearing core. As noted herein, theadditional substrate may take many forms including, but not limited to,scrims (woven or non-woven), films, frims (woven or non-woven), fabrics(woven or non-woven) and other substrate materials as described herein.The adhesive may be permitted to cure, e.g., using heat, drying,molding, pressure, light, cross-linkers or other physical or chemicalmeans to couple the substrate to the core. The presence of the repellenton the core can promote bead formation of the adhesive on the coresurface as noted in more detail below. Bead formation generally canincrease the surface level of adhesive and promote better adhesionbetween the substrate and the core. While it may be desirable to promotebead formation, it can also be desirable to permit a certain level ofadhesive to enter into the porous core to anchor the adhesive in thecore. Depending on the desired level of adherence between the substrateand the core, different amounts of repellent can be added to promotemore adherence or favor less adherence.

In some instances, the prepreg or the core of the article may comprisereinforcing fibers to impart strength to the prepregs or articles. Forexample, the prepreg or core may comprise a plurality of reinforcingfibers. In some embodiments, about 20% to about 80% by weight fibers(based on the weight of the prepreg or the core), more particularlyabout 20% to about 50% by weight fibers, 35% to 60% by weight fibers, orabout 50% to about 80% by weight fibers may be present in the prepreg orthe core. In some instances, the fibers may comprise the same type offibers in the prepreg or core, whereas in other instances, differentfibers may be present in the prepreg or core. In some configurations,fibers comprising a high tensile modulus of elasticity and an averagelength of between about 7 and about 200 mm may be used. Where aplurality of fibers are present in the prepreg or the core, thematerials can be heated above the glass transition temperature of thethermoplastic materials to substantially soften the plastic materials.The softened material can then be provided to one or more consolidationdevices, for example nip rollers, calendaring rolls, double beltlaminators, indexing presses, multiple daylight presses, autoclaves, andother such devices used for lamination and consolidation of sheets andfabrics so that the plastic material can flow and wet out the fibers.The gap between the consolidating elements in the consolidation devicescan be set to a dimension less than that of the unconsolidated web andgreater than that of the web if it were to be fully consolidated, thusallowing the web to expand and remain substantially permeable afterpassing through the rollers. In one embodiment, the gap is set to adimension about 5% to about 10% greater than that of the web if it wereto be fully consolidated. A fully consolidated web refers to a web thatis fully compressed and substantially void free. A fully consolidatedweb would have less than 5% void content and have negligible open cellstructure.

In certain configurations, the fibers may comprise a repellent coatingprior to combining them with the prepreg thermoplastic materials or thethermoplastic materials of the core. For example, the fibers may besprayed, coated with, dipped into or otherwise include a repellentcoating on the surface of the fibers. As noted herein, the repellentnature of the repellent material generally acts to reduce the rate ofabsorption of materials such as fluids into the prepreg or core. In someinstances, fibers comprising a repellent coating can be used along withfibers without any repellent coating. For example, interior portions ofthe prepreg or core may comprise fibers without any repellent coating,and fibers comprising a repellent coating may be added directly to asurface of the prepreg to place such repellent coated fibers inproximity to a surface that can be coupled to a substrate. Where somefibers are coated with a repellent and others fibers are not coated witha repellent, the fiber composition and length may be the same or may bedifferent. While not wishing to be bound by any particular scientifictheory, it may be desirable to increase the overall length of repellentcoated fibers to provide longer and generally continuous coated fibersnear the surface of the prepreg or the core. In other instances, aplurality of repellent coated short fibers (shorter than those presentin the interior of the core) can be used on the surface to assist inbonding to other layers of the article and/or reduction of fluidabsorption into interior portions of the core.

Illustrative types of reinforcing fibers include, but are not limitedto, glass fibers, carbon fibers, graphite fibers, synthetic organicfibers, particularly high modulus organic fibers such as, for example,para- and meta-aramid fibers, nylon fibers, polyester fibers, or any ofthe high melt flow index resins described herein that are suitable foruse as fibers, natural fibers such as hemp, sisal, jute, flax, coir,kenaf and cellulosic fibers, mineral fibers such as basalt, mineral wool(e.g., rock or slag wool), wollastonite, alumina silica, and the like,or mixtures thereof, metal fibers, metalized natural and/or syntheticfibers, ceramic fibers, yarn fibers, or mixtures thereof. In someembodiments, any of the aforementioned fibers can be chemically treatedprior to use to provide desired functional groups or to impart otherphysical properties to the fibers, e.g., may be chemically treated withone or more repellent coatings. The fiber content in the prepreg or coremay be from about 20% to about 90%, more particularly from about 30% toabout 70%, by weight of the prepreg or core. Typically, the fibercontent of the composite varies between about 20% to about 90% byweight, more particularly about 30% by weight to about 80% by weight,e.g., about 40% to about 70% by weight of the composite. The particularsize and/or orientation of the fibers used may depend, at least in part,on the polymer material used and/or the desired properties of theresulting composite. Suitable additional types of fibers, fiber sizesand amounts will be readily selected by the person of ordinary skill inthe art, given the benefit of this disclosure. In one non-limitingillustration, fibers dispersed within a thermoplastic material, formingthe polymer core of a composite, for example, generally have a diameterof greater than about 5 microns, more particularly from about 5 micronsto about 22 microns, and a length of from about 5 mm to about 200 mm;more particularly, the fiber diameter may be from about microns to about22 microns and the fiber length may be from about 5 mm to about 75 mm.

In some embodiments, the prepregs and core layers described herein maycomprise one or more flame retardants. In some instances, the flameretardants may be halogenated flame retardants or substantially halogenfree flame retardants or halogen free flame retardants. For example, theprepregs and core layers can comprise a halogenated flame retardant thatcomprises one of more of F, Cl, Br, I, and At or compounds thatincluding such halogens, e.g., tetrabromo bisphenol-A polycarbonate ormonohalo-, dihalo-, trihalo- or tetrahalo-polycarbonates. In someinstances, the thermoplastic material used in the prepregs and cores maycomprise one or more halogens to impart some flame retardancy withoutthe addition of another flame retardant agent. Where halogenated flameretardants are present, the flame retardant is desirably present in aflame retardant amount, which can vary depending on the other componentswhich are present. For example, the halogenated flame retardant may bepresent in about 0.1 weight percent to about 15 weight percent (based onthe weight of the prepreg or core), more particularly about 1 weightpercent to about 13 weight percent, e.g., about 5 weight percent toabout 13 weight percent. If desired, two different halogenated flameretardants may be added to the prepregs or the cores.

In some instances where the prepregs comprise a substantially halogenfree flame retardant or a halogen free flame retardant, the flameretardant may be (or may comprise) one or more of N, P, As, Sb, Bi, S,Se, Te, F, Cl, Br, I, and At. In some embodiments, the non-halogenatedflame retardant may comprise a phosphorated material so the prepregs andcomposite articles may be more environmentally friendly and comply withrestrictions on hazardous substances (RoHS). Where substantially halogenfree flame retardants are present, the flame retardant is desirablypresent in a flame retardant amount, which can vary depending on theother components which are present. For example, the substantiallyhalogen free flame retardant may be present in about 0.1 weight percentto about 15 weight percent (based on the weight of the prepreg or core),more particularly about 1 weight percent to about 13 weight percent,e.g., about 5 weight percent to about 13 weight percent. If desired, twodifferent substantially halogen free flame retardants may be added tothe prepregs or the cores. In certain instances, the prepregs or corelayers described herein may comprise one or more halogenated flameretardants in combination with one or more substantially halogen freeflame retardants. Where two different flame retardants are present, thecombination of the two flame retardants may be present in a flameretardant amount, which can vary depending on the other components whichare present. For example, the total weight of flame retardants presentmay be about 0.1 weight percent to about 20 weight percent (based on theweight of the prepreg or core), more particularly about 1 weight percentto about 15 weight percent, e.g., about 2 weight percent to about 14weight percent.

In some embodiments, the prepregs and cores may include additionalmaterials or additives to impart desired physical or chemicalproperties. For example, one or more dyes, texturizing agents,colorants, viscosity modifiers, smoke suppressants, synergisticmaterials, lofting agents, particles, powders, biocidal agents, foams orother materials can be mixed with or added to the prepregs or the cores.In some instances, the prepregs or cores may comprise one or more smokesuppressant compositions in the amount of about 0.2 weight percent toabout 10 weight percent. Illustrative smoke suppressant compositionsinclude, but are not limited to, stannates, zinc borates, zincmolybdate, magnesium silicates, calcium zinc molybdate, calciumsilicates, calcium hydroxides, and mixtures thereof. If desired, asynergist material can be present to enhance the physical properties ofthe prepregs or cores. For example, a synergist that enhances therepellent nature of the coating may be present. If desired, a synergistmaterial that enhances flame retardancy may be present. Illustrativesynergist materials include, but are not limited to, sodiumtrichlorobenzene sulfonate potassium, diphenyl sulfone-3-sulfonate, andmixtures thereof.

In other instances, the prepregs or cores described herein may comprisea thermosetting material in a desired amount, e.g., in a minor amountless than about 50 weight percent based on the total weight of theprepreg or core, to impart desired properties to the core. Thethermosetting material may be mixed with the thermoplastic material ormay be added as a coating on one or more surfaces of the prepregs orcores.

In certain embodiments, the prepregs or cores described herein may beporous, non-porous or includes areas which are porous while comprisingother areas which are non-porous. The exact porosity present can varydepending on the intended use of the final article comprising theprepreg or core. In certain embodiments, the prepreg or core cancomprise a porosity greater than 0% by volume, more particularly greaterthan 0% to about 95% by volume, and still more particularly about 30% toabout 70% by volume. While not required, it is also possible that theoverall composite, which is produced using the prepreg or core, isnon-porous or has a porosity within the aforementioned ranges, e.g., theporosity of the composite may generally be greater than 0% to about 95%of the total volume of the composite, more particularly between greaterthan 0% to about 95% by the total volume of the composite, and stillmore particularly between about 30% to about 70% by the total volume ofthe composite. In yet other examples, the prepreg, core or the overallcomposite may comprise a porosity of 0-30%, 10-40%, 20-50%, 30-60%,40-70%, 50-80%, 60-90%, 0-40%, 0-50%, 0-60%, 0-70%, 0-80%, 0-90%,10-50%, 10-60%, 10-70%, 10-80%, 10-90%, 10-95%, 20-60%, 20-70%, 20-80%,20-90%, 20-95%, 30-70%, 30-80%, 30-90%, 30-95%, 40-80%, 40-90%, 40-95%,50-90%, 50-95%, 60-95% 70-80%, 70-90%, 70-95%, 80-90%, 80-95% or anyillustrative value within these exemplary ranges. If desired theporosity of the prepreg, core or the overall composite may be greaterthan 95%, e.g., may be about 96% or 97%. In some instances, as porosityof the prepreg, core or composite increases, it may be desirable to useincreased amounts of repellent material to decrease the absorption rateof any adhesive into the prepreg, core or composite. For example, toreduce the overall basis weight of the article, a core with a porosityof 95% or more can be used along with a repellent material present onthe core surface to reduce absorption of fluid into the highly porouscore.

In producing the prepregs and cores described herein, it may bedesirable to use a wet-laid paper making process. For example, a liquidor fluid medium comprising dispersed material, e.g., thermoplasticmaterials and fibers optionally with any one or more additives describedherein, may be stirred or agitated in the presence of a gas, e.g., airor other gas. The dispersion may then be laid onto a support, e.g., awire screen or other support material, to provide a substantiallyuniform distribution of fibers over the laid down material. To increasefiber dispersion and/or uniformity, the stirred dispersion may compriseone or more active agents, e.g., anionic, cationic, or non-ionic suchas, for example, those sold under the name ACE liquid by IndustrialSoaps Ltd., that sold as TEXOFOR® FN 15 material, by Glover ChemicalsLtd., and those sold as AMINE Fb 19 material by Float-Ore Ltd. Theseagents can assist in dispersal of air in the liquid dispersion. Thecomponents can be added to a mixing tank, flotation cell or othersuitable devices in the presence of air to provide the dispersion. Whilean aqueous dispersion is desirably used, one or more non-aqueous fluidsmay also be present to assist in dispersion, alter the viscosity of thefluid or otherwise impart a desired physical or chemical property to thedispersion or the prepreg, core or article.

In certain instances, after the dispersion has been mixed for asufficient period, the fluid with the suspended materials can bedisposed onto a screen, moving wire or other suitable support structureto provide a web of laid down material. Suction or reduced pressure maybe provided to the web to remove any liquid from laid down material toleave behind the thermoplastic material and any other materials that arepresent, e.g., fibers, additives, etc. The resulting web can be dried,consolidated, pressed, lofted, laminated, sized or otherwise processedfurther to provide a desired prepreg, core or article. In someinstances, the repellent material may be added to the web prior todrying, consolidation, pressing, lofting, laminating, sizing or otherfurther processing to provide a desired prepreg, core or article. Inother instances, the repellent material may be added to the websubsequent to drying, consolidation, pressing, lofting, laminating,sizing or other further processing to provide a desired prepreg, core orarticle. While wet laid processes may be used, depending on the natureof the thermoplastic material and other materials present, it may bedesirable to instead use an air laid process, a dry blend process, acarding and needle process, or other known process that are employed formaking non-woven products. In some instances, the repellent material issprayed onto the surface of the prepreg or core after the prepreg orcore has hardened to some degree by passing the board underneath aplurality of coating jets that are configured to spray the repellentmaterial at about a ninety degree angle to the prepreg or core surface.

In certain configurations, the prepregs and cores described herein maybe present without any repellent coating or material, and a substrate tobe coupled to the prepregs or core may comprise a repellent materialthat is effective to reduce the absorption rate of the adhesive. Theexact nature of the substrate may vary depending on the intended use ofthe formed article, but in some instances the substrate can be athermoplastic film, an elastomeric film, a metal foil, a thermosettingcoating, an inorganic coating, a fiber based scrim, a non-woven fabric,and a woven fabric. If desired, the substrate may comprise a limitingoxygen index greater than about 22, as measured per ISO 4589-2, firstedition, 1996, to enhance at least one of the flame, smoke, heat releaseand gaseous emissions characteristics as described, for example, incommonly assigned U.S. Pat. No. 7,682,697. In some instances, it may bedesirable to use a porous substrate so that the repellent materialand/or any adhesive can penetrate into the pores (to at least somedegree) and provide enhanced bonding between the prepreg or core and thesubstrate. As noted in more detail below, both the prepreg or core andthe substrate may comprise a repellent material if desired.

In some embodiments, the resulting composite or board that comprises theprepreg or core may have a desired basis weight. For example, theoverall basis weight of the resulting board may vary from about 200 gsmto about 3000 gsm, more particularly about 800 gsm to about 2000 gsm,for example about 900 gsm to about 1500 gsm. In some instances, theoverall basis weight can be reduced when a repellent material is used ascompared to when no repellent material is present, e.g., where arepellent material is present, the basis weight of the board can bereduced by 30%, 40%, 50% or more and still provide suitable physicalproperties

In certain examples and referring to FIG. 1, a composite articlecomprising a base layer 110 (which may be a prepreg or core but fordiscussion purposes is referred to as a core below) with a substrate 130disposed on the layer 110 is shown. For illustration purposes, arepellent layer 115 and an adhesive layer 120 is shown, though an actuallayer may not be present but, instead, the materials may be sprayed onto form discontinuous areas of repellent and/or adhesive. The repellentmaterial 115 is added to the core 110 prior to disposal of the adhesive120 to repel the adhesive from being absorbed into the core, e.g., toreduce the absorption rate of adhesive into the core. The substrate 130is then added onto the adhesive 120, and the article 100 may be cured toprovide a final formed article. The core 110 may comprise one or morethermoplastic materials and reinforcing fibers as noted herein inconnection with prepregs and core materials. The repellent material 115may be any one or more of the repellent materials described herein. Thesubstrate 130 may be any of those substrates described herein, e.g., athermoplastic film, an elastomeric film, a metal foil, a thermosettingcoating, an inorganic coating, a fiber based scrim, a non-woven fabric,and a woven fabric. The adhesive 120 may comprise suitable adhesivesincluding, but not limited to, hot melt adhesives, thermoplasticadhesives, thermoset adhesives or other suitable adhesives such as, forexample, polyolefin adhesives, ethylene-vinyl acetate based adhesives,polyamide adhesives, polyester adhesives, polyurethane adhesives,thermoplastic polyurethane adhesives, styrene block copolymer adhesives,polycarbonate adhesives, fluoropolymeric adhesives, silicone adhesives,silicone rubber adhesives, elastomeric adhesives, pyrrole adhesives orother suitable adhesives. The adhesive may be present in many differentforms including, liquid and solid forms, resin form, rosin form or otherforms and may optionally contain additives such as waxes, plasticizers,antioxidants, flame retardants, UV stabilizers, dyes, colorants,pigments, biocidal agents, antistatic agents, fillers, particles,powders, whiskers, fibers or other desired additives. The adhesive, forexample, may be water based or may be oil based. In some instances, theadhesive used may be “thin” or substantially non-viscous, e.g., may flowat room temperature. The presence of a repellent permits the use ofliquid based adhesives with good retention on the surfaces of thevarious components of the articles prior to curing or processing.

In certain configurations, it may be desirable to add another substrateto the substrate coupled to the prepreg or core. Referring to FIG. 2A,an article 200 is shown comprising a prepreg or core 210 coupled to asubstrate 220. In the article 200, no adhesive or repellent coating ispresent between the core 210 and the substrate 220, but if desired, oneor more of an adhesive and/or repellent may be used. For example, thethermoplastic material of the core 210 may be softened or melted tocouple the substrate 220 to the core 210. The substrate 220 comprises arepellent coating 225 on a surface or some portions thereof. An adhesive230 (or other fluid material) is disposed on the repellent 225, which iseffective to retain a substantial amount, e.g., greater than 50%, 60%,70%, 80% or 90% of the disposed adhesive, on the surface of thesubstrate 220. If desired, another substrate 240 may be coupled to thesubstrate 220 through the adhesive 230 (as shown in FIG. 2B) to providean article 250. The substrates 220, 250 may be the same or may bedifferent. In some instances, additional repellent and adhesive may bedisposed on the substrate 250 to permit addition of another substrate onthe article 250. In this manner, a desired number of substrate layersmay be added to a prepreg or core layer to provide a final article.

In some instances, it may be desirable to couple two or more prepreg orcore layers to increase the overall thickness of the article. Forexample and referring to FIG. 3A, an article 300 comprising prepreg orcore layers 310, 320 is shown. The core layers 310, 320 are coupled toeach other through a repellent layer 312. The repellent layer 312 may beeffective to reduce the flow rate of the thermoplastic material in eachof the layers 310, 320. This reduction can result in better adhesion ofthe two thermoplastic layers 310, 320 to each other in the article 300.If desired, one or more adhesives may be present between prepreg or corelayers 310, 320. For example and referring to FIG. 3B, an adhesive layer332 is shown as being disposed on a repellent layer 312. The repellentlayer 312 is effective to retain substantially more adhesive of theadhesive layer 332 on the surface of the core 310 to permit enhancedbonding of the core 310 to the core 320. Additional prepreg or corelayers may be coupled to the articles 300 or 350 to increase the overallthickness and number of prepreg or core layers present in a finalarticle.

In certain configurations, it may be desirable to include a repellentlayer or coating between each of the different components present in anarticle. Referring to FIG. 4, an article 400 is shown comprising aprepreg or core 410 coupled to a substrate 420 through a repellent layer415. The substrate 420 is coupled to an additional substrate 430 througha repellent layer 425 and an adhesive layer 427. Additional substratesmay be coupled to the substrate 420 using additional repellent layersand/or adhesive layers. In some instances, 2, 3, 4, 5 or more additionalsubstrates may be coupled to the substrate 420.

In some configurations, one or more substrates may be coupled to eachside of a prepreg or core layer. Referring to FIG. 5, a compositearticle 500 comprising a base layer 510 (which may be a prepreg or corebut for discussion purposes is referred to as a core below) with asubstrate 530 disposed on the layer 510 is shown. For illustrationpurposes, a repellent layer 515 and an adhesive layer 520 are shown,though an actual layer may not be present but, instead, the materialsmay be sprayed on to form discontinuous areas of repellent and/oradhesive. The repellent material 515 is added to the core 510 prior todisposal of the adhesive 520 to repel the adhesive from being absorbedinto the core, e.g., to reduce the absorption rate of adhesive into thecore. The substrate 540 is then added onto the adhesive 520. On theother side of the core 510 a repellent layer 555 is added followed by anadhesive layer 560. An additional substrate 570 is added on the adhesivelayer 560. While the substrate 570 is shown as being coupled to the core510 through layers 555, 560, if desired, the layers 555, 560 may beomitted and the substrate 570 may be directly coupled to the core 550without the use of any adhesive or repellent material. The article 500may be cured to provide a final formed article. The core 510 maycomprise one or more thermoplastic materials and reinforcing fibers asnoted herein in connection with prepregs and core materials. Therepellent materials 515, 555 may be any one or more of the repellentmaterials described herein and may be the same or may be different. Thesubstrates 530, 570 may be any of those substrates described herein,e.g., a thermoplastic film, an elastomeric film, a metal foil, athermosetting coating, an inorganic coating, a fiber based scrim, anon-woven fabric, and a woven fabric and may be the same or may bedifferent. The adhesive layers 520, 560 may comprise suitable adhesivesincluding, but not limited to, hot melt adhesives, thermoplasticadhesives, thermoset adhesives or other suitable adhesives such as, forexample, polyolefin adhesives, ethylene-vinyl acetate based adhesives,polyamide adhesives, polyester adhesives, polyurethane adhesives,thermoplastic polyurethane adhesives, styrene block copolymer adhesives,polycarbonate adhesives, fluoropolymeric adhesives, silicone adhesives,silicone rubber adhesives, elastomeric adhesives, pyrrole adhesives orother suitable adhesives. The adhesive layers 520, 560 may be the sameor may be different. The adhesive may be present in many different formsincluding, liquid and solid forms, resin form, rosin form or other formsand may optionally contain additives such as waxes, plasticizers,antioxidants, flame retardants, UV stabilizers, dyes, colorants,pigments, biocidal agents, antistatic agents, fillers, particles,powders, whiskers, fibers or other desired additives. In some instances,the adhesive used may be “thin” or substantially non-viscous, e.g., mayflow at room temperature. The adhesives in the layers 520, 560 mayindependently be water based adhesives or oil based adhesives. In someinstances, one of the layers 520, 560 comprises a water based adhesiveand the other layer comprises an oil based adhesive. In other instances,each of the layers 520, 560 may be a water based adhesive or an oilbased adhesive. The presence of a repellent permits the use of liquidbased adhesives with good retention on the surfaces of the variouscomponents of the articles prior to curing or processing. If desired,different amounts of repellent material and/or adhesive may be used oneach side of the core 510.

In certain configurations, it may be desirable to add another substrateto the substrate coupled to the prepreg or core. Referring to FIG. 6A,an article 600 is shown comprising a prepreg or core 610 coupled to asubstrate 620. In the article 600, no adhesive or repellent coating ispresent between the core 610 and the substrate 620, but if desired, oneor more of an adhesive and/or repellent may be used. For example, thethermoplastic material of the core 610 may be softened or melted tocouple the substrate 620 to the core 610. A second substrate 660 isdisposed on another surface of the core 610. Each of the substrates 620,660 comprises a repellent coating 625, 665, respectively, on a surfaceor some portions thereof. Adhesive layers 630, 670 are disposed on therepellent layers 625, 665, respectively. The exact amount of repellentmaterial and adhesive material used can vary and may vary between thedifferent layers, 625, 630, 665, 670. In some instances, enoughrepellent material is present on each of the substrates 620, 660 to beeffective to retain a substantial amount, e.g., greater than 50%, 60%,70%, 80% or 90% of the disposed adhesive, on the surface of thesubstrates 620, 660. If desired, another substrate 680 may be coupled tothe substrate 620 through the adhesive 630 (as shown in FIG. 6B) toprovide an article 690. The substrates 620, 660 and 680 may be the sameor may be different. In some instances, additional repellent andadhesive may be disposed on the substrate 680 to permit addition ofanother substrate on the substrate 680. In this manner, a desired numbersubstrate layers may be added to a prepreg or core layer to provide afinal article.

In some instances, it may be desirable to couple two or more prepreg orcore layers to increase the overall thickness of the article. Forexample and referring to FIG. 7, an article 700 comprising prepreg orcore layers 710, 720 is shown. The core layers 310, 320 are coupled toeach other through a repellent layer 712. The repellent layer 712 may beeffective to reduce the flow rate of the thermoplastic material in eachof the layers 710, 720. This reduction can result in better adhesion ofthe two thermoplastic layers 710, 720 to each other in the article 700.In some instances, the repellent layer 712 can be omitted and the cores710, 720 can be directly stacked onto each other without any interveningrepellent material. If desired, one or more adhesives may be presentbetween prepreg or core layers 710, 720. For example, an adhesive layermay be present and disposed on the repellent layer 712 if desired. Onthe other surface of the core layer 710 is a repellent layer 760 and anadhesive layer 765, which are used to couple a substrate 770 to the corelayer 710. Additional prepreg or core layers may be coupled to thearticle 700 to increase the overall thickness and number of prepreg orcore layers present in a final article.

In certain configurations, it may be desirable to include a repellentlayer or coating between each of the different components present in anarticle comprising a plurality of substrates. Referring to FIG. 8, anarticle 800 is shown comprising a prepreg or core 810 coupled to asubstrate 820 through a repellent layer 815. The substrate 820 iscoupled to an additional substrate 830 through a repellent layer 825 andan adhesive layer 827. Additional substrates may be coupled to thesubstrate 820 using additional repellent layers and/or adhesive layers.In some instances, 2, 3, 4, 5 or more additional substrates may becoupled to the substrate 820. The article 800 also comprises anothersubstrate 850 coupled to another surface of the prepreg or core 810through a repellent layer 845 and an adhesive layer 847.

In some instances, it may be desirable to couple two or more substratesusing a repellent material to enhance bonding between the substrates.Referring to FIG. 9, a first substrate 910 is coupled to a secondsubstrate 920 through a repellent material 915. As noted in connectionwith FIGS. 1-8, the repellent material 915 may not actually be presentas a layer but instead may be sprayed, coated or otherwise disposed onone or both of the substrates 910, 920. The repellent material 915 maybe effective to reduce the level at which the two substrates “melt” intoeach other. This effect may permit alteration of processing conditionsto provide a tighter bond between the substrates. While not shown, anadhesive material may be disposed on the substrates prior to coupling toeach other to further enhance coupling of two substrates 910, 920.

In some embodiments, the fiber orientation in one of the substrates 910,920 may be different from the fiber orientation in the other substrate.For example, the fibers in the substrate 920 may be oriented in themachine direction, e.g., at 0 degrees, and the fibers in the substrate910 may be oriented in the cross direction, e.g., at 90 degrees toprovide a bidirectional fiber orientation, e.g., 0/90 fibers. Otherangles, e.g., 45 degrees, 60 degrees, 75 degrees, etc. are alsopossible. In addition, the fibers in the two substrates 910, 920 may beoriented in the same direction or angle if desired. In articlescomprising two or more substrates on two or more surfaces of a prepregor core layer, the substrates on each surface may provide abi-directional orientation or other desired fiber orientation. Inproducing such articles, a first tape or roll of material comprisingfibers oriented in one direction may be placed on a core layercomprising a repellent material and optionally an adhesive material. Thearticle may then be cured if desired. Alternatively, a repellentmaterial and optionally an adhesive may be disposed on the first tape,and a second tape or roll of material comprising fibers oriented in aselected direction may be disposed on the repellent material and/oradhesive material. The article may then be cured to provide a finalarticle comprising a selected fiber orientation in the different tapelayers. In some embodiments, a single tape comprising 0/90 fibers in onelayer may be disposed on a prepreg or core followed by application of arepellent treatment to the disposed tape.

In some embodiments, the fibers of the tapes or rolls of material may betreated with a repellent material prior to formation of the tape. Forexample, fibers may be coated or sprayed with a repellent material andthen can be embedded in a thermoplastic material to provide a tapecomprising thermoplastic material in combination with the repellenttreated fibers. If desired, each tape used may comprise repellenttreated fibers or one of the tapes may comprise repellent treatedfibers.

In some embodiments, the substrates which can be added to the prepregsand cores described herein may take many forms including, but notlimited to, films, frims (woven or non-woven), scrims (woven ornon-woven), foils, fabrics (woven or non-woven) or other suitablematerials. Where a fiber based scrim is used, the scrim may comprise oneor more of glass fibers, aramid fibers, graphite fibers, carbon fibers,inorganic mineral fibers, metal fibers, metalized synthetic fibers, ametallized inorganic fibers, polyacrylonitrile, p-aramid, m-aramid,poly(p-phenylene2,6,benzobisoxazole), poly(ether-imide), poly(phenylenesulfide), polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, and polyvinyl chloride. Where the substratetakes the form of a film, the film may comprise one or more ofpoly(ether imide), poly(ether ketone), poly(ether-ether ketone),poly(phenylene sulfide), poly(arylene sulfone), poly(ether sulfone),poly(amide-imide), poly(1,4-phenylene), polycarbonate, nylon, andsilicone. The substrate may also comprise unsaturated polyurethanes,vinyl esters, phenolics, epoxies, gypsum, calcium carbonate, mortar,minerals containing cations selected from Ca, Mg, Ba, Si, Zn, Ti and Aland other metal species.

In some instances, the thermoplastic composite articles described abovecan be used in, but not limited to, building infrastructure, buildingproducts (e.g., boards, window frames, drywall substitutes, interior orexterior wall panels, roof underlayments, floor underlayments, backerboard, etc.), aircraft, train and naval vessel side wall panels, ceilingpanels, cargo liners, office partitions, elevator shaft lining, ceilingtiles, recessed housing for light fixtures and other such applicationsthat are currently made with honeycomb sandwich structures,thermoplastic sheets, and flame retardant panels. The composite sheetscan be molded into various articles using methods known in the artincluding, for example, pressure forming, thermal forming, thermalstamping, vacuum forming, compression forming, and autoclaving. Thecombination of high stiffness to weight ratio, ability to bethermoformed with deep draw sections (if desired), end of liferecyclability, acoustics and desirable low flame spread index, heatrelease, smoke density and gas emission properties make the porousfiber-reinforced thermoplastic composite a more desirable product thanthe products currently being used. Particularly desirable applicationsof the articles find use in recreational vehicles and other vehicles asthe repellent coating can reduce the overall weight of the articleswhile still permitting retention of binding strength and/or resistanceto delamination. Other desirable uses are those where high moisture orhigh humidity environments are encountered as the repellent coatedarticles are effective at preventing water absorption. For example, thearticles can be used as backer boards for shower panels or asunderlayments for flooring or roofing as the repellent material on theboards acts to deter water absorption. In some instances, the boards areanti-fungal and/or anti-bacterial as the boards can be designed toinclude materials that do not support fungal or bacterial growth. Forexample, where the boards comprise a polyolefin thermoplastic core andglass reinforcing fibers along with a perfluoro repellent materialtreatment, mold growth is generally not supported. In addition, thetemperature insensitive nature of articles described herein provides foreasier assembly of panels and products without the adverse temperaturevariability processing commonly encountered with existing articles. Theuse of lighter weight panels reduces overall cost, increases fuelefficiency and permits the use of less expensive and complicatedassembly equipment.

In some embodiments, the articles described herein may be moresusceptible to bending while retaining desired performancecharacteristics. The enhanced resistance to delamination may permitbending of the articles to provide rounded shapes, e.g., roundedcorners, rounded noses or other rounded features. In some instances, thearticles provided herein may be formed into a generally solid body andthen desired areas may be cut out or rounded out. For example, a wallboard may be formed and spaces for windows may be routed out without anysubstantial delamination of the various components which are coupled toeach other. In other instances, a wall board may be formed and bent toprovide a circular shower shape without any hard corners as such shapesmay be more aesthetically desirable and the lack of any joints in theboard reduces the likelihood of water penetration behind the board.

In certain embodiments, the articles described herein may comprise arepellent material to provide a repellency grade number of 3 or higheras tested by the ISO 23232 test method dated 2009. The ISO 23232 testmethod can be used to determine the ability of a fluid, e.g., water orwater/alcohol mixtures, to be retained on a surface of a material. Thehigher the repellency grade number, the more resistant the boardgenerally is to fluid absorption.

In using the ISO 23232 test method, test liquids are added to thesurface of a material at a volume of about 0.05 mL in three differentlocations (usually about 4 cm apart). The drops are added at a height ofabout 0.6 cm above the surface. The drop is observed for about 10seconds for penetration. The drop shape is compared to the shapes inFIG. 10. It is desirable that the drop shape resembles the “A” or “B”shape as drops with the “C” shape and the “D” shape representpenetration into the article. If no penetration occurs, e.g., the dropshave the “A” shape or the “B” shape in FIG. 10, then the next gradeliquid is added as shown in Table 1 below.

TABLE 1 Solution Composition Surface Tension Aqueous SolutionWater:Isopropanol (by at 25 deg. C. Repellency Grade Number volume)(dyn/cm) 0 100:0  72.0 1 98:2  59.0 2 95:5  50.0 3 90:10 42.0 4 80:2033.0 5 70:30 27.5 6 60:40 25.4 7 50:50 24.5 8 40:60 24.0This process is repeated from solution 0 to solution 8 until penetration(if any) is observed. For example, if penetration is observed withsolution 4, then the surface would be considered to have a repellencygrade of 3 under the ISO 23232 test method. If penetration is observedwith solution 7, then the surface would be considered to have arepellency grade of 6 under the ISO 23232 test method.

In other instances, the prepregs, cores and articles described hereinmay include a repellent treatment effective to retain a fluid on itssurface for at least 5 minutes as tested using the same procedureoutlined in the ISO 23232 test method. This test is referred to incertain instances as the “5-minute modified ISO 23232 test method.” Forexample, if the board is rated a repellency grade of 3 under the5-minute modified ISO 23232 test method, then droplets of solution #3 inTable 1 above, when added to the surface of the board using the ISO23232 test method, are retained on the surface (in the “A” or “B” shape)for at least 5 minutes.

In certain embodiments, the prepregs, cores and composite articlesdescribed herein can be used as a floor underlayment or a roofunderlayment. Referring to FIG. 11, an illustration of a house 1100showing a roof surface comprising core layers as described herein isshown. The cores can be installed as panels 1110-1140 with overlappingjoints. Each panel may be, for example, about 4 feet by about 8 feet andabout 2-4 mm in thickness. The panels can be adhered, nailed orotherwise attached to the underlying roof surface and then covered withasphalt shingles or other suitable roofing materials, e.g., aluminum,clay tiles, slate, etc. Instead of installing individual panels, a boltof material comprising the core can be used to drape a continuous sheetof core layer across the roof surface. Additional core layer runs can bepulled across the first run in a similar manner as existing roofingunderlayments, e.g., tar paper, used in roofing applications. The corelayers, if desired, can be directly attached to the back of asphaltshingles (or other roofing materials such as aluminum or tiles) to speedup installation of the roofing materials. In some instances, thematerials of the core layers are selected so that they will soften (to asmall degree) in their use environment. Softening can permit differentcore layers to “melt” into each other and form a generally continuousbarrier under the roofing materials. This barrier, due to its repellentnature from the presence of a repellent material, can prevent water fromreaching underlying sheathing. It is a desirable attribute that the corelayers, when used as roofing underlayments, can act as water/icebarriers and reduce the likelihood of subsurface penetration by water.

Similar to the use of the materials as roofing underlayments, the corelayers can be added as a floor underlayment to reduce noise, dampenvibrations and provide some insulation. For example, the porous opencell structure of the core layers can act as an effective insulatorbetween flooring materials and any underlying sub-floor. This insulativeeffect can reduce heat transfer/loss and can decrease the passage ofsound from one floor of a building to another floor of a building.

In certain instances, the prepregs or cores described herein can be usedin surface applications in environments exposed to high moisture.Illustrative applications include using the prepregs, cores and articlesas back boards for tile, for shower panels and other areas of bathrooms,kitchens or rooms where high moisture may be experience continuously orintermittently. Referring to FIG. 12, a top view of a shower stall 1200is shown. The shower stall comprises panels 1232, 1234 and 1236 whichmay be acrylic or other materials, or in alternative designs, varioustile materials can be used instead. A base structure 1210, e.g., studs,concrete block or other members, is present and attached to prepregs orcores (or composite articles) 1222, 1224 and 1226 which comprise arepellent treatment as described herein. The presence of the repellenttreatment on the panels 1222, 1224 and 1226 permits the use of lessadhesive to attach the panels 1232, 1234 and 1236. In addition, thewater repellent nature of the panels 1222, 1224 and 1226 acts to determoisture penetration to the underlying base structure 1210. While theshower stall 1200 is shown as having various corners, the bendability ofthe prepregs and cores can permit construction of a rounded shower stallwith a single continuous panel comprising the prepregs or cores and asingle overlying panel or acrylic or other materials.

In certain configurations, the prepregs, cores and articles describedherein can be used as exterior sheathing, interior sheathing or exterioror interior wall applications. For example, the cores can replaceexterior plywood or OSB sheathing and provide greater resistance towater penetration that traditional wood substrate materials. In otherinstances, the cores can be used in place of plaster board or gypsumboard. Paint or other surface coatings such as stucco, plaster and thelike can be added directly to the core to provide a finished surface.Referring to FIG. 13, an illustration of various components that can beused in finishing a wall structure are shown. The wall structure 1300comprises an interior surface 1305 and an exterior surface 1370. Theinterior surface coating 1305 can take many forms including paint,plaster, stucco, etc. The interior coating 1305 can be disposed on aboard 1310 such as drywall, backer board, greenboard or one or theprepregs, cores or composite articles described herein, e.g., one with arepellent material. Adjacent to the inner layer 1310 is an insulationlayer 1210, which typically takes the form of cellulose, fiberglass,isocyanate or other insulation materials. A layer 1330 is adjacent tothe insulation layer 1320. The layer 1330 may comprise a prepreg, coreor composite article with a repellent material. A vapor barrier 1340underlies the layer 1330 and is positioned adjacent to woods studs 1350,e.g., is stapled to the wood studs 1350. If desired, additionalinsulation can be placed between the studs 1350, e.g., fiberglass battinsulation may be placed between the studs. On the outside of thebuilding, another insulation layer 1355 can be present. If desired, anadditional vapor barrier 1360, e.g., in the form or a sheet or tape, canbe placed on the insulation layer 1355. An optional horizontal rainscreen 1365 can be present between the vapor barrier 1360 and exteriorsheathing or siding 1370. Where the sheathing or siding 1370 is to becovered by an additional material, e.g., brick, vinyl siding, aluminumsiding, etc., the sheathing may be one or more of the prepregs describedherein to deter entry of water into other components of the wall system1300. It will be recognized by the person of ordinary skill in the art,given the benefit of this disclosure, that not all components of thewall system 1300 need be present. For example, a wall system comprisinga first core layer attached to wood studs or concrete block on theinside of the structure, and a second core layer attached to the woodstuds or concrete block on the outside of the structure can beimplemented. The second core layer can be covered with a vapor barrierand siding to prevent moisture from penetrating the wall assembly. Otherconfigurations using one or more core layers in a wall or buildingassembly will be recognized by the person of ordinary skill in the art,given the benefit of this disclosure.

In some instances, the prepregs or cores described herein can belaminated to each other to provide a structural member such as a stud,joist, truss or other weight bearing or structural members present in abuilding. Various different open porous cores can be laminated orotherwise joined to each other, e.g., using an adhesive or othermaterials, and can be sized to provide a suitable dimension, e.g., canbe sized and used as a dimensional wall stud or used in construction ofengineered trusses. In some instances, the prepregs or cores can belaminated or sealed to existing wood studs or trusses (or otherstructural members) to seal them from the external environment and/orprovide additional weight bearing support. Additional applications wherethe prepregs and cores with a repellent treatment are used as structuralmembers will be recognized by the person of ordinary skill in the art,given the benefit of this disclosure.

In certain configurations, the prepregs, core layers and compositearticles with repellent materials as described herein can be used foranti-fungal and/or anti-bacterial applications. For example, thematerials can be used in kitchen or bathroom countertops, as structuralsupport materials for sinks or toilets, as wall boards in clean rooms orforensic facilities, in settings for growing microbiological organismsand in other settings where it is desired to prevent or deter fungal orbacterial growth. The prepregs and cores can desirably be used wheremold is likely to occur. As at least some configurations of the prepregsand cores do not include any materials which support mold growth, theprepregs and cores can provide some mold resistance without the need toadd any fungicide or other biocidal agents. The ability to deter moldgrowth without the addition of antifungal agents to the prepregs orcores is a substantial attribute of the prepregs and cores describedherein.

Certain specific examples are described below to illustrate further someof the novel aspects and uses of the technology described herein.

Example 1

A 25 gsm scrim, e.g., an aramid or PET scrim, can be coupled to athermoplastic core layer comprising polypropylene and glass fibers. Arepellent treatment, e.g., perfluoro material treatment or otherrepellent material treatment, may be provided on the 25 gsm scrim priorto coupling to the core layer to permit use of the lighter weight scrimwhile still providing desired adhesion between the core layer and thescrim. The overall basis weight of the resulting board may vary fromabout 800 gsm to about 1200 gsm.

Example 2

An article can be produced comprising a thermoplastic core comprising athermoplastic material and reinforcing fibers. The article may alsoinclude a scrim or other substrate coupled to the core. A repellenttreatment, e.g., perfluoro material treatment or other repellentmaterial treatment. may be provided to the core of the substrate (orboth), and the article may be coupled to a structural interiorcomponent, e.g., foam or metal reinforced foam, to provide a wall panelsuitable for use in recreational vehicles, as wall cubicles or otheruses. One or more decorative skins may be added to the surfaces of thepanel to provide for enhanced aesthetics. Skins exposed to weather maycomprise, for example, a fiberglass reinforced polyethylene resin whichis generally seamless. Skins on the interior may comprise, for example,a decorative paper or other material.

Example 3

Liquid urethane was disposed on a scrim surface of an article comprisinga fiber-reinforced thermoplastic core (polypropylene and glass fiberswith an overall basis weight of about 1100 gsm) and a 20 gsmpolyethyleneterephthalate scrim coated with a repellent. Adhesive wasdisposed at a rate of 17 grams per square foot.

As shown in FIGS. 14A and 14B, the liquid urethane remained almostentirely on the surface of the repellent treated porous composite (FIG.14B) and formed a plurality of liquid urethane beads across the span ofthe surface. The white bars present in FIGS. 14A and 14B mask aninternal label used on the boards.

Referring to FIGS. 15A and 15B, microscopic images of boards producedwithout (FIG. 15A) and with (FIG. 15B) repellent treatment show thatboards produced with a repellent treatment have adhesive beads which“stand up” on the surface. These results are consistent with enhancedretention of fluid, e.g., adhesive, on the surface when a repellenttreatment is added to the surface prior to the addition of adhesive.

Example 4

A hot melt polyurethane was disposed on a scrim surface of an articlecomprising a fiber-reinforced thermoplastic core (polypropylene andglass fibers with an overall basis weight of about 1100 gsm) and a 20gsm polyethyleneterephthalate scrim coated with a repellent. Adhesivewas disposed at a rate of 17 grams per square foot.

As shown in FIGS. 16A and 16B, the polyurethane remained almost entirelyon the surface of the repellent treated porous composite (FIG. 16B) andformed a plurality of liquid urethane beads across the span of thesurface. The white bars present in FIGS. 16A and 16B mask an internallabel used on the boards.

Referring to FIGS. 17A and 17B, microscopic images of boards producedwithout (FIG. 17A) and with repellent treatment (FIG. 17B) show thatboards produced with a repellent treatment have a generally continuouslayer across the top surface without any substantial absorption into theinterior of the core. These results are consistent with enhancedretention of fluid, e.g., adhesive, on the surface when a repellenttreatment is added to the surface prior to the addition of adhesive.

Example 5

Liquid urethane was disposed on a scrim surface of an article comprisinga fiber-reinforced thermoplastic core (polypropylene and glass fiberswith an overall basis weight of about 1100 gsm) and a 20 gsmpolyethyleneterephthalate scrim coated with a repellent. Adhesive wasdisposed at a rate of 17 grams per square foot.

As shown in FIGS. 18A and 18B, the liquid urethane remained almostentirely on the surface of the repellent treated porous composite (FIG.18B) and formed a plurality of liquid urethane beads across the span ofthe surface. The white bars present in FIGS. 18A and 18B mask aninternal label used on the boards.

Referring to FIGS. 19A and 19B, microscopic images of boards producedwithout (FIG. 19A) and with (FIG. 19B) repellent treatment show thatboards produced with a repellent treatment have adhesive beads which“stand up” on the surface. These results are consistent with enhancedretention of fluid, e.g., adhesive, on the surface when a repellenttreatment is added to the surface prior to the addition of adhesive.

Example 6

Arboc liquid urethane was disposed on a scrim surface of an articlecomprising a fiber-reinforced thermoplastic core (polypropylene andglass fibers with an overall basis weight of about 1100 gsm) and a 20gsm polyethyleneterephthalate scrim coated with a repellent. Adhesivewas disposed at a rate of 17 grams per square foot.

As shown in FIGS. 20A and 20B, the liquid urethane was partiallyabsorbed into the board but a substantial amount remained on the surfaceof the repellent treated porous composite (FIG. 20B) and formed aplurality of liquid urethane beads across the span of the surface. Thewhite bars present in FIGS. 20A and 20B mask an internal label used onthe boards.

Referring to FIGS. 21A and 21B, microscopic images of boards producedwithout (FIG. 21A) and with (FIG. 21B) repellent treatment show thatboards produced with a repellent treatment have adhesive beads which“stand up” on the surface, whereas the non-treated boards absorb almostall of the adhesive within the board interior. These results areconsistent with enhanced retention of fluid, e.g., adhesive on thesurface when a repellent treatment is added to the surface prior to theaddition of adhesive.

Example 7

CFC liquid urethane was disposed on a scrim surface of an articlecomprising a fiber-reinforced thermoplastic core (polypropylene andglass fibers with an overall basis weight of about 1100 gsm) and a 20gsm polyethyleneterephthalate scrim coated with a repellent. Adhesivewas disposed at a rate of 17 grams per square foot.

Referring to FIGS. 22A and 22B, microscopic images of boards producedwith free expansion of the urethane adhesive (FIG. 22A) and constrainedexpansion of the urethane adhesive (FIG. 22B). Constrained expansionsforces the adhesive into the interior of the board after promotingsubstantial spread of the adhesive across the glue interface.

When introducing elements of the examples disclosed herein, the articles“a,” “an,” “the” and “said” are intended to mean that there are one ormore of the elements. The terms “comprising,” “including” and “having”are intended to be open-ended and mean that there may be additionalelements other than the listed elements. It will be recognized by theperson of ordinary skill in the art, given the benefit of thisdisclosure, that various components of the examples can be interchangedor substituted with various components in other examples.

Although certain aspects, examples and embodiments have been describedabove, it will be recognized by the person of ordinary skill in the art,given the benefit of this disclosure, that additions, substitutions,modifications, and alterations of the disclosed illustrative aspects,examples and embodiments are possible.

1-80. (canceled)
 81. A composite article comprising: a core comprising aweb of open celled structures defined by random crossing over ofreinforcing materials held together by a thermoplastic material, thecore comprising a repellent treatment on a surface of the core, in whichthe repellent treatment is effective to decrease absorption of a fluidinto voids of the core; and a substrate disposed on the core.
 82. Thearticle of claim 81, in which the reinforcing materials comprisereinforcing fibers.
 83. The article of claim 82, in which thereinforcing fibers are present from about 20 weight percent to about 80weight percent based on the weight of the core.
 84. The article of claim82, in which the reinforcing fibers comprise metal fibers, metalizedinorganic fibers, metallized synthetic fibers, glass fibers, carbonfibers, aramid fibers, ceramic fibers and combinations thereof.
 85. Thearticle of claim 81, further comprising an adhesive layer disposed onthe at least one surface comprising the repellent treatment.
 86. Thearticle of claim 85, in which the adhesive layer comprises a polyolefinadhesive, an ethylene-vinyl acetate adhesive, a polyamide adhesive, apolyester adhesive, a polyurethane adhesive, a thermoplasticpolyurethane adhesive, a styrene block copolymer adhesive, apolycarbonate adhesive, a fluoropolymeric adhesive, a silicone adhesive,a silicone rubber adhesive, an elastomeric adhesive, or a pyrroleadhesive.
 87. The article of claim 85, in which the substrate comprisesa film, a frim, a scrim, a foil, a woven fabric or a non-woven fabric.88. The article of claim 85, in which the repellent material iseffective to render the adhesive temperature and/or viscosityinsensitive.
 89. The article of claim 81, in which the thermoplasticmaterial comprises polyethylene, polypropylene, polystyrene,acrylonitrylstyrene, butadiene, polyethyleneterephthalate,polybutyleneterephthalate, polybutylenetetrachlorate, polyvinylchloride, polyphenylene ether, polycarbonates, polyestercarbonates,thermoplastic polyesters, polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof.
 90. The article of claim 81, further comprising aflame retardant in the core or the substrate or both.
 91. A compositearticle comprising: a core comprising a web of open celled structuresdefined by random crossing over of reinforcing materials held togetherby a thermoplastic material; and a substrate disposed on the core, thesubstrate comprising a repellent treatment on at least one surface ofthe substrate, the repellent treatment effective to decrease absorptionof a fluid into the substrate.
 92. The article of claim 91, in which thereinforcing materials comprise reinforcing fibers.
 93. The article ofclaim 92, in which the reinforcing fibers are present from about 20weight percent to about 80 weight percent based on the weight of thecore.
 94. The article of claim 92, in which the reinforcing fiberscomprise metal fibers, metalized inorganic fibers, metallized syntheticfibers, glass fibers, carbon fibers, aramid fibers, ceramic fibers andcombinations thereof.
 95. The article of claim 91, further comprising anadhesive layer disposed on the at least one surface comprising therepellent treatment.
 96. The article of claim 95, in which the adhesivelayer comprises a polyolefin adhesive, an ethylene-vinyl acetateadhesive, a polyamide adhesive, a polyester adhesive, a polyurethaneadhesive, a thermoplastic polyurethane adhesive, a styrene blockcopolymer adhesive, a polycarbonate adhesive, a fluoropolymericadhesive, a silicone adhesive, a silicone rubber adhesive, anelastomeric adhesive, or a pyrrole adhesive.
 97. The article of claim95, in which the substrate comprises a film, a frim, a scrim, a foil, awoven fabric or a non-woven fabric.
 98. The article of claim 95, inwhich the repellent material is effective to render the adhesivetemperature and/or viscosity insensitive.
 99. The article of claim 91,in which the thermoplastic material comprises polyethylene,polypropylene, polystyrene, acrylonitrylstyrene, butadiene,polyethyleneterephthalate, polybutyleneterephthalate,polybutylenetetrachlorate, polyvinyl chloride, polyphenylene ether,polycarbonates, polyestercarbonates, thermoplastic polyesters,polyimides, polyamides, polyetherimides,acrylonitrile-butylacrylate-styrene polymers, amorphous nylon,polyarylene ether ketone, polyphenylene sulfide, polyaryl sulfone,polyether sulfone, poly(1,4phenylene) compounds, silicones andcombinations thereof.
 100. The article of claim 91, further comprising aflame retardant in the core or the substrate or both. 101-220.(canceled)